Abstract:In this study, we develop a roasting method for removing arsenic from sulfide copper-arsenic-containing materials. The object of the study was fine dust from copper smelting production of the following composition (wt%): 34.89 – Zn; 20.02 – Cu; 17.74 – Pb; 17.07 – Fe; 7.12 – As; 0.92 – Sb; 0.69 – Sn; 0.63 – Ca; 0.42 – Mo; and 0.34 – K. The chemical composition of the materials was analyzed using an SHIMADZU EDX-7000 energy dispersive X-ray fluorescence spectrometer and a Bruker D8 Advance diffractometer. The roasting process was carried out in a laboratory tube furnace at a temperature of 550–800°C for 60–120 minutes with the addition of 25–50% of FeS 2 to the charge. Optimal conditions for reducing residual arsenic in the calcine to less than 0.3 wt% were identified: a temperature of 750–800°C, a duration of 1.5–2.0 h (in an inert atmosphere), and the use of 30 wt% of pyrite concentrate in the charge. Arsenic removal to the gas phase reached 91–96%. It is shown that in order to reduce the processing temperature to 600°C, it is necessary to add a reducing agent (coke fines) to the mixture of copper smelting dust with pyrite or increase the proportion of pyrite in the test charge to 50 wt% and hold the mixture for 1.5–2.0 h under inert atmosphere (argon and nitrogen) or low-oxygen blast. Arsenic removal to the gas phase reached 97%. X-ray spectral analysis of the residue deposited on the cooled ends of quartz tubes following the release of gases formed during roasting revealed that this material is predominantly (up to 93%) composed of arsenic. The resulting calcine contained 94 wt% of iron, zinc, copper and lead compounds. Therefore, the calcine obtained during the roasting of fine dust from copper smelting production is suitable for returning to the copper production process.

Removal of Arsenic During Iron Extraction from Waste Copper Slag

Ultrasonic-enhanced selective arsenic removal and sulfide conversion from iron slag

Iron and copper recovery from copper slags through smelting with waste cathode carbon from aluminium electrolysis

Removal and immobilization of arsenic from copper smelting wastewater using copper slag by in situ encapsulation with silica gel

Effect of injection of different gases on removal of arsenic in form of dust from molten copper smelting slag prior to recovery process

Leaching and removal of arsenic with waste acids from arsenic pre-removed dusts discharged from furnaces for pyrometallurgical refining of copper

Removal of arsenic from “Dirty acid” wastewater via Waelz slag and the recovery of valuable metals

Minimization and stabilization of smelting arsenic-containing hazardous wastewater and solid waste using strategy for stepwise phase-controlled and thermal-doped copper slags

Efficient and safe disposition of arsenic by incorporation in smelting slag through copper flash smelting process

Arsenic removal from copper slag matrix by high temperature sulfide-reduction-volatilization

Experimental Study on Separation of Iron and Arsenic from Copper Sulfate Solution

Arsenic removal from arsenic-containing copper and cobalt slag using alkaline leaching technology and MgNH4AsO4 precipitation

Separation of silicon and iron in copper slag by carbothermic reduction-alkaline leaching process

Recovery of value-added products from copper slag by pyrometallurgy: Transfer and structure of arsenic compounds

Arsenic removal from acid extraction solutions of copper smelting flue dust

Co-treatment of copper smelting flue dust and arsenic sulfide residue by a pyrometallurgical approach for simultaneous removal and recovery of arsenic

Effective Removal of Arsenic from Copper Matte by Sodium Carbonate

Effect of roasting parameters on arsenic removal from copper smelting dust

Determination of occurrence and leaching toxicity of arsenic in copper flash smelting slags

An efficient approach to utilize copper smelting slag: Separating nonferrous metals and reducing iron oxide at high temperature

Strategies for arsenic pollution control from copper pyrometallurgy based on the study of arsenic sources, emission pathways and speciation characterization in copper flash smelting systems