Abstract:Alloying of corrosion-resistant austenitic steels with nitrogen is widely used in production to stabilize austenite and to improve the strength and other properties of the metal. The possibility of alloying titanium-containing steels with nitrogen by introducing nitrogen into the melt is not possible, as it causes formation of the coarse defects in steel during casting and solidification of the metal (twisting of the peel, large nitride inclusions, accumulations of nitrides, etc.). The method of high-temperature gas nitriding can be alternative to liquid-phase nitriding for alloying austenitic titanium-containing chromium-nickel steels with nitrogen in order to increase their strength properties. In this work, we investigated the possibility of increasing the strength characteristics of thin-sheet austenitic corrosion-resistant Cr – Ni – Ti (Kh18N12T type) steel, containing 1.5 % and 3 % of titanium, through the use of solid-phase high-temperature nitriding. The nitriding was carried out at a temperature of 1000 – 1100 °С in an atmosphere of pure nitrogen for 5 or 8 hours. The average mass fraction of nitrogen in the samples after nitriding for 5 hours was 0.6 % and 0.7 % for the steels with 1.5 and 3 % of titanium, respectively, and after nitriding for 8 hours – 0.8 % and 0.9 %. It was shown that high-temperature nitriding followed by annealing provides a significant (by 2 – 3 times) increase in the metal strength characteristics compared with the state before nitriding, but reduces the ductility. Ductility of the steel is restored during final processing. For Kh18N12Т type steel with 1.5 % of titanium, an increase in the yield strength is obtained – by 3.3 times (from 180 to 600 MPa), strength – by 1.8 times (from 540 to 970 MPa), with a relative elongation of 28 %. An additional increase in strength properties was not found for the steel with 3 % titanium. The obtained results show the possibility of obtaining thin-sheet titanium-containing high-nitrogen steel (or products from it, for example, thin-walled pipes) by applying solid-phase high-temperature nitriding.

Stability of Structure and Properties of Nitrogen High-Strength Austenitic Steels Under Cyclic Thermal and Mechanical Loads

Research on the thermal plasticity of the 18Mn-18Cr-0.77N-2Mo high nitrogen austenitic stainless steel

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Structure and Mechanical Properties of High-Strength Structural Steels

Effect of the Temperature of Shock-Wave Loading on Structure and Phase Transformations in Nitrogen-Containing Austenitic Cr–Mn–Ni Steel

STRUCTURE AND MECHANICAL PROPERTIES OF AUSTENITIC Cr – Ni – Ti STEELS AFTER HIGH-TEMPERATURE NITRIDING

Cryogenic Investigations into the Effect of Impact-Oscillatory Loading on Changes in the Mechanical Properties and Structural Condition of VT23M Two-Phase Titanium Alloy

Microstructure evolution of austenitic stainless steels under high-cycle-fatigue loading at deep cryogenic temperature

Effect of Heat Treatment on Mechanical Properties and Microstructure of Advanced High-Strength Steel

Microstructural Characterization and Mechanical Property Evaluation of High Nitrogen Martensitic Stainless Steel Subjected to Heat Treatment

Low-temperature mechanical properties and microstructural stability of high-nitrogen and low-nickel austenitic stainless steel

Role of the martensitic microstructure in the stabilized residual stresses under cyclic loading and in the fatigue behavior of two steels

Microstructure and Property of Nitrogen-Alloyed High Manganese Austenitic Steel under High Strain Rate Tension

Cryogenic Work-Hardening Behavior for a Metastable Austenitic Stainless Steel at Liquid Nitrogen Temperature

A Study of Decomposition of Supercooled Austenite in High-Strength Medium-Carbon Complexly Alloyed Cold-Resistant Steels

Martensitic-austenitic steels for the fabrication of equipment and other articles in instrument making

Metallurgical aspects of dispersion nitride hardening of high-carbon steel. Message 1. The effect of austenizing heating and tempering parameters on the phase redistribution of nitrogen and vanadium in steels

High Temperature In Situ Optical Observation and Structural Optimization Numerical Simulation of High Nitrogen Steel (Cr18Mn18N)

Influence of Tempering and Cryogenic Treatment on Retained Austenite and Residual Stresses in Carbonitrided 18CrNiMo7-6 Low Alloy Steel

Thermomechanical processing model and abnormal microstructure evolution of high-nitrogen stainless steel X30CrMoN15-1

Cyclic Deformation Response of Austenitic Ni-based Alloy: Mechanical Behavior, Internal Stress Evolution and Microstructural Feature