Low-temperature mechanical properties and microstructural stability of high-nitrogen and low-nickel austenitic stainless steel

Guifang Xu,Wenhui Xu,Rui Luo,Dongsheng Li,Xiaonong Chen

DOI: https://doi.org/10.13251/j.issn.0254-6051.2017.02.001

2017-01-01

Abstract:In order to evaluate low-temperature properties and microstructural stability of two high-nitrogen austenitic stainless steels H1 and H2 with nitrogen content of 0.614% and 0.529%, respectively, the tensile and impact properties of the steels at low temperature were investigated, their fracture morphologies were observed by scanning electron microscope, the phase composition and microstructure of the two tested steels near tensile and impact fracture were analyzed by X-ray diffraction and TEM.The experimental results show that tensile strength and yield strength of the samples increase monotonously with the decrease of testing temperature, and elongation as well as reduction of area decreases gradually, the strength of the samples increases with the increase of nitrogen content but the ductility decreases.Low-temperature impact test results indicate that the impact toughness decreases with the increase of nitrogen content which has little effect on the ductile-brittle transition temperature of steels H1 and H2 taking place at -122 ℃ and -123 ℃, respectively.XRD and TEM results indicate that the steels have superior stability of microstructure and no martensitic transformation and precipitation of nitride occur during the tensile and impact test.