Abstract:An Al‐containing MIL‐53 metal‐organic framework with very high surface area (SBET=1130 m2.g−1, N2 sorption) was used as sacrificial template to prepare a nickel‐alumina‐based catalyst (Ni0AlMIL) highly active and stable in the reaction of dry reforming of methane (DRM). The procedure consisted in impregnating the activated (solvent free) MIL‐53 sample with a nickel precursor solution, then calcining the material to remove the organic linkers and subsequently reducing it to form the reduced nickel active phase. At the step of calcination, this procedure results in the formation of a porous uniform spinel phase with Ni nanospecies embedded in the alumina‐based matrix, as deduced from XRD, TPR and TEM analyses. This leads after reduction to a porous lamellar γ‐Al2O3 material with small Ni0 nanoparticles homogeneously dispersed and stabilized within the support. The performances of this catalyst in DRM are better than those of two reference Ni/alumina catalysts prepared for comparison by conventional nickel impregnation of two preformed alumina supports: a first one obtained by calcination of MIL‐53 (AlMIL) and a second one consisting of a commercial γ‐Al2O3 batch (AlCOM). Under steady state conditions at a temperature of 650 °C and a pressure of 1 bar, the higher CH4 and CO2 conversions (till 3 times higher than on Ni0/AlCOM), high catalytic stability (no loss of activity after 13–100 h) and higher selectivity towards DRM (H2:CO products ratio remaining at 1) on Ni0AlMIL compared to the other catalysts is believed to come from the particularly strong interaction between the nickel and alumina phases generated by using the unique high specific surface of the parent MOF support to deposit nickel. This creates an intimate mixing favorable to a persisting interaction of the nickel nanoparticles with the alumina support in the reduced material. The lamellar shape of the γ‐Al2O3 composing the catalyst and its remaining high specific surface may also contribute to the excellent Ni resistance to sintering and in turn to the inhibition of carbon nanotubes formation during the reaction.

Ni/Al2O3-La2O3 catalysts synthesized by a one-step polymerization method applied to the dry reforming of methane: effect of precursor structures of nickel, perovskite and spinel

A highly active Ni catalyst supported on Mg-substituted LaAlO3 for carbon dioxide reforming of methane

The Ni Catalyst Supported on the FSP-made Transition Metal (Co, Mn, Cu or Zn) Doped La2O3 Material for the Dry Reforming of Methane

Improving Coking Resistance and Catalytic Performance of Ni Catalyst from LaNiO3 Perovskite by Dispersion on SBA-15 Mesoporous Silica for Hydrogen Production by Steam Reforming of Ethanol

High Performance of Mg–La Mixed Oxides Supported Ni Catalysts for Dry Reforming of Methane: the Effect of Crystal Structure

Dry reforming of methane over nickel catalysts supported on magnesium aluminate spinels

Ordered mesoporous Ni-La2O3/Al2O3 catalysts towards efficient plasma-assisted dry reforming of methane

Highly Dispersed Ni Nanoparticles Supported by Porous Al2O3 Rods for Catalytic Dry Reforming of Methane

One‐pot Synthesis of Ordered Mesoporous NiCeAl Oxide Catalysts and a Study of Their Performance in Methane Dry Reforming

Preparation and evaluation of the LaCu1-xNixO3 (x = 0, 0.1, 0.3, 0.5 and 0.7) perovskite catalysts for total oxidation of methane

Highly dispersed Ni/Al2O3 catalysts for dry reforming of methane prepared by alkaline-induced adsorption process

Enhancement of CO2 Methanation over La-Modified Ni/SBA-15 Catalysts Prepared by Different Doping Methods

Porous Nickel‐Alumina Derived from Metal‐Organic Framework (MIL‐53): A New Approach to Achieve Active and Stable Catalysts in Methane Dry Reforming

Performance of Ni-Based Catalysts with La Promoter for the Reforming of Methane in Gasification Process

Studies on nickel-based catalysts for carbon dioxide reforming of methane

Methane dry reforming over activated carbon supported Ni-catalysts prepared by solid phase synthesis

Improving Anti-Coking Properties of Ni/Al2O3 Catalysts via Synergistic Effect of Metallic Nickel and Nickel Phosphides in Dry Methane Reforming

Catalytic CO2 Reforming of Methane over Perovskite Noble Metals

Highly Active and Stable Lanthanum‐doped Core–Shell‐structured Ni@SiO2 Catalysts for the Partial Oxidation of Methane to Syngas

Facile Route for Synthesizing Ordered Mesoporous Ni–Ce–Al Oxide Materials and Their Catalytic Performance for Methane Dry Reforming to Hydrogen and Syngas

Ni/x%Nb2O5/Al2O3 Catalysts Prepared via Coprecipitation-Wet Impregnation Method for Methane Steam Reforming