Boric acid as converter material for semiconductor neutron detector- A GEANT4 simulation study

Manoj Kumar Parida,S. Tripura Sundari,K. Prabakar

DOI: https://doi.org/10.1016/j.nima.2019.162978

2020-01-01

Abstract:<p>Monte Carlo based GEANT4 simulations have been carried out to estimate the efficiency (<span class="math"><math>η</math></span>) of thermal neutron detection with boric acid (H₃BO₃) as a converter material. Different geometries of detector configurations — planar stack, sphere, cylinder and cuboid were considered and their efficiency were computed for relevant geometric parameters along with different  ¹⁰B enrichment (<span class="math"><math>BE</math></span>) levels content in boric acid, with Low Level Discriminator (LLD) value fixed at 300 keV. The planar stack configuration detector was designed by replicating two dimensional detector units (DUs) – each consisting of boric acid as a converter material and Silicon (Si) as a detector material – in the third dimension. The simulation carried out for varied layer thicknesses (<span class="math"><math>0.25μm</math></span> to <span class="math"><math>10μm</math></span>) of boric acid showed that efficiency (<span class="math"><math>η</math></span>) increased with increasing thickness, reached a maximum at a critical thickness (<span class="math"><math>tsc</math></span>) and thereafter found to decrease. Typically, at a critical thickness of <span class="math"><math>∼</math></span>3.5<span class="math"><math>μm</math></span>, the <span class="math"><math>η</math></span> for 100% <span class="math"><math>BE</math></span> content in boric acid was found to be 15.96% for 30 DUs. For the case of sphere, cylinder and cuboid of boric acid embedded in Si, the simulations were performed for diameter and width both varying from <span class="math"><math>0.5μm</math></span> to <span class="math"><math>9.5μm</math></span> in steps of <span class="math"><math>0.5μm</math></span>. In particular for cylinder and cuboid geometries, the depth was also varied from <span class="math"><math>25μm</math></span> to <span class="math"><math>275μm</math></span> with a step size of <span class="math"><math>25μm</math></span>. In all these configurations <span class="math"><math>η</math></span> was found to increase initially and was maximum at a critical diameter and width of <span class="math"><math>∼</math></span>8–9<span class="math"><math>μm</math></span>, and thereafter it was found to reduce. Apart from the simulated <span class="math"><math>η</math></span> estimation, histogram plots depicting the energy deposited in Si detector region by the generated charged particles (⁷Li <span class="math"><math>=</math></span> 0.839 MeV and <span class="math"><math>α=1.47MeV</math></span>) upon thermal neutron interaction in boric acid have also been studied for various geometrical parameters such as thickness, diameter and width of detector.</p>