Abstract:Large-scale nonequilibrium molecular dynamics simulation is used to study the effect of grain size and Cr segregation at the twin boundary (TB) on the spalling fracture mechanism of nickel based alloys. In particular, loading waves are designed so that the maximum tensile stress first appears in the grain interior for all the crystals with different grain sizes. In contrast to traditional understandings, no monotonous relationship between the spall strength and the grain size appears in our results. The spall strength is found to depend on the wave attenuation distance measured from the first maximum tensile stress position to the spalled TB as well as the accompanied microstructure evolutions. The number of spalling plane increases with the increase of TB or the decrease of the grain size. As the grain size continues to decrease, a greater impact strength is required to cause spallation fracture at multiple TBs. In this case, the spall strength becomes insensitive to the first maximum tensile stress position. With the increment of solute atom concentration, the number of the spalling plane increases when the solution is segregated. But it decreases when the solution is uniformly distributed. Such a result is explained by segregation-enhanced energy dissipation and interactions between the waves and the microstructures nearby TBs. In particular, the shock wave would induce a local lattice reorientation nearby the TB depending on its segregation degree and the lattice reorientation would modify the slip manner of stacking faults and, thus, affect void nucleation and growth. The lattice reorientation would also contribute to the generation of sub-grain boundaries inside the grains in terms of the movement of stacking faults. Void nucleation at the sub-GB is the main cause of fracture at the grain interior.

Effect of grain size on fatigue cracking at twin boundaries in a CoCrFeMnNi high-entropy alloy

Effect of Twin Boundary Density on Mechanical Behavior of Al0.1CoCrFeNi High-Entropy Alloy by Molecular Dynamics Simulation

Microstructure sensitivity of the low cycle fatigue crack initiation mechanisms for the Al 0.3 CoCrFeNi high entropy alloy: in-situ SEM study and crystal plasticity simulation

Low cycle fatigue behaviors of CrCoNi medium-entropy alloy with different grain sizes

Transition of twinning behavior in CoCrFeMnNi high entropy alloy with grain refinement

Microstructure relevant fatigue short crack propagation behavior of Al 0.3 CoCrFeNi high entropy alloy: in-situ SEM study

Fatigue crack growth behavior in CoCrFeMnNi high entropy alloy with harmonic structure topology

Deformation mechanisms of CoCrFeMnNi high-entropy alloy under low-cycle-fatigue loading

Effect of microstructure and local stress on small crack initiation and propagation paths in coarse‐grained FeCrAl alloys

Influence of grain structure and precipitates on fatigue crack propagation behaviors of Al- x Cu-1.2Li-X alloys

Influence of twinning thickness on the mechanical properties of crystalline-amorphous dual-phase CoCrFeNiMn high entropy alloy

Hierarchical Grain Size and Nanotwin Gradient Microstructure for Improved Mechanical Properties of a Non-Equiatomic CoCrFeMnNi High-Entropy Alloy

A review on the fatigue cracking of twin boundaries: Crystallographic orientation and stacking fault energy

Atomic Simulations of Grain Structures and Deformation Behaviors in Nanocrystalline CoCrFeNiMn High-Entropy Alloy

Effects of grain size on the precipitation pathway and mechanical properties of (CoCrFeNi)94Ti2Al4 high entropy alloy

Effect of Grain Size on the Tribological Behavior of CoCrFeMnNi High Entropy Alloy

Grain size dependent deformation behavior of a metastable Fe40Co20Cr20Mn10Ni10 high-entropy alloy

Influence of the twin boundary and Cr segregation on the spalling of Ni-base alloys by large-scale molecular dynamic simulations

Ultra-long life fatigue behavior of a high-entropy alloy

Nonmonotonic effect of chemical heterogeneity on interfacial crack growth at high-angle grain boundaries in Fe-Ni-Cr alloys

Influences of grain size and twin boundary on the tensile properties of nanocrystalline face-centered cubic Cu50Ni50 alloy