Abstract:Two different morphologies of martensite in dual-phase (DP) steel were obtained through two processing routes. In the first method, the steel was water quenched from a fully austenitic state, followed by intercritical annealing (IA). In the second method, the steel was water quenched, cold rolled, and then subjected to intercritical annealing (C-IA). For IA and C-IA steels, the intercritical temperatures varied from 735 C-degrees to 765 C-degrees to obtain different fractions of ferrite. To understand the effect of ferrite content, morphology, and the orientation of ferrite/austenite on martensitic transformation, a combination of scanning electron microscopy, electron backscattered diffraction, and dilatometric tests were conducted. It was observed that layered martensite presented in IA samples, and blocky martensite appeared only at prior austenite boundaries at 765 C-degrees. In C-IA samples, equiaxed martensite grains were present, which become coarser by elevating the temperature to 765 C-degrees. In IA samples, martensitic transformation was much faster than in C-IA samples; the difference in martensitic transformation rate is particularly significant at lower annealing temperatures. Carbon enrichment of the partial austenite had a converse effect on the martensitic transformation at 745 C-degrees in both samples. The highest transformation rate was recorded in IA samples at 745 C-degrees among all IA and C-IA samples. The ferrite/martensite in IA samples maintained Kurdjumov-Sachs orientation relationship (K-S OR) with prior austenite and selected the same variant in the same block. Whereas, in polygonal samples, ferrite/martensite had an irrational OR with the prior austenite, no variant selection appeared in ferrite and martensite grains. Martensite nucleation accelerated on the ferrite surface when it had a K-S OR with the matrix grain, forming a low-energy interface with the ferrite. In contrast, ferrite surfaces irrationally oriented with the matrix grain did not promote martensite nucleation. This was likely due to the large misorientation and higher carbon build-up near the boundary during intercritical holding. The lower activation energy for martensitic nucleation in IA samples compared to C-IA samples resulted in an accelerated rate of martensite transformation in IA samples.

Development of In-situ Orientation Mapping and Microstructure Observation System for Ferrite/Austenite and Martensitic Transformations in Steel

In Situ Observation of Bainite to Austenite Transformation of Microalloyed High Strength Steel During Simulated Welding Cycle

In Situ Observation of Γ → Α Transformation During Hot Deformation in an Fe-Ni Alloy by an X-ray Diffraction Method

In-situ Observation of Solid Phase Transformation of a low Carbon Steel

In Situ Observation of Martensitic Phase Transformation in Low Carbon Steel Containing Cu

In Situ Observation of Acicular Ferrite Formation and Grain Refinement in Simulated Heat Affected Zone of High Strength Low Alloy Steel

In Situ Observation of Austenite–ferrite Interface Migration in a Lean Mn Steel During Cyclic Partial Phase Transformations

In situ observation of bainite transformation of low carbon Si-Mn steel

The Influence of Intercritical Temperature, Ferrite-Austenite Morphology, and Orientation Relationship on Martensitic Transformation in Dual Phase Steels

In Situ Observation of the Grain Growth Behavior and Martensitic Transformation of Supercooled Austenite in NM500 Wear-Resistant Steel at Different Quenching Temperatures

Microstructural Characterization of Martensite Formed in High-carbon Steel Based on Rodrigues-Frank Space

In Situ Observation of Bainitic Transformation Behavior in Medium Carbon Bainitic Steel

Development and application of a high-temperature imaging system for in-situ scanning electron microscope

Microstructural Evolution of High Cr Ferrite/martensite Steel after Deformation in Metastable Austenite Zone

In Situ Austenite–martensite Interface Mobility Study During Annealing

In-situ Observation of Phase Transformation During Heat Treatment Process of High-Carbon Bainitic Bearing Steel

Early Martensitic Transformation in a 0.74C–1.15Mn–1.08Cr High Carbon Steel

The In Situ Observation of Phase Transformations During Intercritical Annealing of a Medium Manganese Advanced High Strength Steel by High Energy X-Ray Diffraction

In situ 3D crystallographic characterization of deformation-induced martensitic transformation in a metastable Fe–Cr–Ni austenitic alloy by X-ray microtomography

In situ observation of the austenite to ferrite transformation in low-carbon steels from different initial phases at defined cooling rates

An In Situ Synchrotron Dilatometry and Atomistic Study of Martensite and Carbide Formation during Partitioning and Tempering