Abstract:Two different morphologies of martensite in dual-phase (DP) steel were obtained through two processing routes. In the first method, the steel was water quenched from a fully austenitic state, followed by intercritical annealing (IA). In the second method, the steel was water quenched, cold rolled, and then subjected to intercritical annealing (C-IA). For IA and C-IA steels, the intercritical temperatures varied from 735 C-degrees to 765 C-degrees to obtain different fractions of ferrite. To understand the effect of ferrite content, morphology, and the orientation of ferrite/austenite on martensitic transformation, a combination of scanning electron microscopy, electron backscattered diffraction, and dilatometric tests were conducted. It was observed that layered martensite presented in IA samples, and blocky martensite appeared only at prior austenite boundaries at 765 C-degrees. In C-IA samples, equiaxed martensite grains were present, which become coarser by elevating the temperature to 765 C-degrees. In IA samples, martensitic transformation was much faster than in C-IA samples; the difference in martensitic transformation rate is particularly significant at lower annealing temperatures. Carbon enrichment of the partial austenite had a converse effect on the martensitic transformation at 745 C-degrees in both samples. The highest transformation rate was recorded in IA samples at 745 C-degrees among all IA and C-IA samples. The ferrite/martensite in IA samples maintained Kurdjumov-Sachs orientation relationship (K-S OR) with prior austenite and selected the same variant in the same block. Whereas, in polygonal samples, ferrite/martensite had an irrational OR with the prior austenite, no variant selection appeared in ferrite and martensite grains. Martensite nucleation accelerated on the ferrite surface when it had a K-S OR with the matrix grain, forming a low-energy interface with the ferrite. In contrast, ferrite surfaces irrationally oriented with the matrix grain did not promote martensite nucleation. This was likely due to the large misorientation and higher carbon build-up near the boundary during intercritical holding. The lower activation energy for martensitic nucleation in IA samples compared to C-IA samples resulted in an accelerated rate of martensite transformation in IA samples.

In Situ Austenite–martensite Interface Mobility Study During Annealing

In Situ Observation of Austenite–ferrite Interface Migration in a Lean Mn Steel During Cyclic Partial Phase Transformations

Interface Migration Between Martensite and Austenite During Quenching and Partitioning (Q&P) Process

A Preliminary In-situ TEM Study of Martensite/Austenite Interface Migration in an Fe-20Ni-5.4Mn Alloy

Austenite Formation and Cementite Dissolution During Intercritical Annealing of a Medium-Manganese Steel from a Martensitic Condition

Analysis of Interface Migration and Isothermal Martensite Formation for Quenching and Partitioning Process in a Low-Carbon Steel by Phase Field Modeling

An in Situ Transmission Electron Microscopy Study of Interface Growth During Martensitic Transformation in an Fe–Ni–Mn Alloy

In Situ Observation of Martensitic Phase Transformation in Low Carbon Steel Containing Cu

The In Situ Observation of Phase Transformations During Intercritical Annealing of a Medium Manganese Advanced High Strength Steel by High Energy X-Ray Diffraction

An Overview of the Cyclic Partial Austenite-Ferrite Transformation Concept and Its Potential

Austenite/Ferrite Interface Migration and Alloying Elements Partitioning: an Overview

Mobility of Various Intervariant Interfaces in 18R Martensite in a Cu-Zn-Al Alloy Part I: In-situ Observations

Combined Martensite and Bainite Formation from Austenite Decomposition in HSLA Steel

Microstructural Evolution of a Low-Carbon Steel during Application of Quenching and Partitioning Heat Treatments after Partial Austenitization

Kinetics of Carbon Enrichment in Austenite during Partitioning Stage Studied via In-Situ Synchrotron XRD

In Situ Observation of Bainite to Austenite Transformation of Microalloyed High Strength Steel During Simulated Welding Cycle

Excess Carbon Enrichment in Austenite During Intercritical Annealing

Effect of Intercritical Annealing on Microstructural Evolution and Properties of Quenched & Partitioned (Q&P) Steels

Effect of Annealing Temperature and Time on Microstructure Evolution of 0·2c–5mn Steel During Intercritical Annealing Process

The Influence of Intercritical Temperature, Ferrite-Austenite Morphology, and Orientation Relationship on Martensitic Transformation in Dual Phase Steels

Atom-probe tomographic and dilatometric studies of phase-transformations after inter-critical annealing of a low-carbon dual-phase steel