Microstructural homogeneity, mechanical properties, and wear behavior of in situ Mg2Si particles reinforced Al–matrix composites fabricated by hot rolling

Dongtao Wang,Haitao Zhang,Hiromi Nagaumi,Pinfeng Jia,Jianzhong Cui
DOI: https://doi.org/10.1016/j.jmrt.2019.12.020
IF: 6.267
2020-03-01
Journal of Materials Research and Technology
Abstract:<p>In situ Mg<sub>2</sub>Si particles often show coarse and irregular morphologies in Al–matrix composites, which results in inhomogeneous microstructures and poor mechanical properties. This leads to poor deformation ability in Mg<sub>2</sub>Si particles reinforced Al–matrix composites. Herein, a refined process exploiting refined Mg<sub>2</sub>Si particles was developed to enhance microstructure homogeneity after hot rolling in an Al-11.73%Mg-6.63%Si composite. The hot-rolled sheet reduces the macroscopic cracking on the edge when the Mg<sub>2</sub>Si particles of the as-cast microstructure are refined by the addition of phosphorus. The refined Mg<sub>2</sub>Si particles in the as-cast state shows further size reduction and exhibits homogeneous distribution by hot rolling (reduction of 76%). The microstructure also shows uniform deformation zones, subgrains and high-density dislocation regions via hot rolling. The homogeneous deformation microstructure results in needle-like, high-density precipitates after artificial aging and decreases the stress concentration of load bearing, which is beneficial to the tensile properties and wear resistance of the composite. The wear behavior of the composites improves with Mg<sub>2</sub>Si-particle refinement and microstructural homogeneity.</p>
What problem does this paper attempt to address?