Microstructural, hardness, and wear properties of Mg 2 Si-reinforced Al matrix in-situ composites produced by low superheat casting

Tolga Ozkan,Ibrahim Tutuk,Serhat Acar,Ridvan Gecu,Kerem Altug Guler
DOI: https://doi.org/10.1016/j.mtcomm.2023.107937
IF: 3.8
2024-01-01
Materials Today Communications
Abstract:In this study, Mg 2 Si-reinforced A356 and A413 aluminum matrix composites were fabricated by low superheat casting using AM50 magnesium alloy as a source for the in-situ formation of Mg 2 Si particles. AM50 was added to each Al alloy at 5 %, 10 %, and 15 % ratios, respectively. Casting temperatures for these composites were 650 °C for A356 and 620 °C for A413. After the production, the as-cast samples were reheated to 580 °C and quenched. The microstructure and hardness properties of both as-cast and reheated samples were investigated and wear tests were carried out on the as-cast specimens. As the AM50 ratio increased, the morphology of Mg 2 Si became finer, and polygonal primary particles were precipitated in the A356 and A413 matrix as-cast composites. The formation of in-situ Mg 2 Si particles improved the hardness of the composites by up to 47 %. The hardness values reached 94 and 93 HB in the A356–5 and A413–15 specimens, respectively. Besides, wear rates were decreased by up to 55 % in the Mg 2 Si-reinforced composites compared to the unreinforced alloys.
materials science, multidisciplinary
What problem does this paper attempt to address?