Abstract:In the present investigation, aluminum metal matrix composites (AMMs) reinforced with aluminum nitride (AlN) nanoparticulates at different volumetric ratios of (0, 0.5, 1, 1.5, and 2 vol.%) were manufactured via a microwave-assisted powder metallurgy technique. The morphological, physical, mechanical, and electrochemical properties of the produced billets were examined to reflect the impact of the successive addition of AlN into the aluminum (Al) matrix. The morphological analysis revealed the high crystalline patterns of the formation of the Al-AlN composites. The microstructural analysis confirmed the presence of the elemental constituents of Al and AlN particles in the fabricated composites, showing an enhanced degree of agglomeration in conjunction with the additional amount of AlN. Positive behavior exhibited by the micro- and nanohardness was noticeable in the Al-AlN composites, especially at the ultimate concentration of AlN in the Al matrix of a 2 vol.%, where it reached 669.4 ± 28.1 MPa and 659.1 ± 11 MPa compared to the pure Al metal at 441.2 ± 20 MPa and 437.5 ± 11 MPa, respectively. A declining trend in the compressive strength was recorded in the reinforced Al samples. The corrosion resistance of the AlN-reinforced Al metal matrix was estimated at 3.5 wt.% NaCl using electrochemical impedance spectroscopy and potentiodynamic polarization. The results reveal that the inclusion of 2.0 vol.%AlN led to the lowest corrosion rate.

Fabrication and Characterization of Aluminum Nitride Nanoparticles by RF Magnetron Sputtering and Inert Gas Condensation Technique

Characterization of aluminum nitride thin films by ion beam analysis techniques

Experimental Analysis and Characterization of High-Purity Aluminum Nanoparticles (Al-NPs) by Electromagnetic Levitation Gas Condensation (ELGC)

Facile synthesis of monodisperse aluminum nitride microspheres

Fabrication and Characterization of Nbn, Aln and Nbn/Aln/Nbn on Mgo Substrates

Structural and Mechanical Properties of Radiofrequency Ar-N2 Plasma Nitrided Aluminium

Synthesis and optical properties of hexagonal aluminum nitride nanocrystals

Preparation of Aln Thin Films for Film Bulk Acoustic Resonator Application by Radio Frequency Sputtering

Aln Nanorings

Characterisation of Aluminium Nitride Films and Surface Acoustic Wave Devices for Microfluidic Applications

Preparation of Aln Films by Pulsed Laser Deposition Using Sintered Aluminum Nitride and Elemental Aluminum As Raw Materials

Comparison of aluminum nitride thin films prepared by magnetron sputter epitaxy in nitrogen and ammonia atmosphere

Synthesis of Aluminum Nitride Powders from A Plasma-Assisted Ball Milled Precursor Through Carbothermal Reaction

Fabrication of Aln Thin Films on Different Substrates at Ambient Temperature

Effect of AlN on the Mechanical and Electrochemical Properties of Aluminum Metal Matrix Composites

Evolution of Aluminum Nitride Nanostructures from Nanoflower to Thin Film on Silicon Substrate by Direct Nitridation of Aluminum Precursor

Effect of solvent and processing condition on structure and morphology of aluminum nitride nanopowders fabricated by electrical explosion of wire (EEW)

Synthesis of aluminum nitride by nitridation of γ-Al 2O3 nanopartlcles in flowing ammonia

Synthesis of Aluminum Nitride Nanocrystals and Platelets

AlN Nanoparticles Prepared Through a Gelation-Polymerization Process

Growth of Spontaneous Nucleation AlN Crystals by Al-Base Alloy Evaporation in Nitrogen Atmosphere