Abstract:Silica aerogel has been formed using CO2 gas as the gelation agent through the low-cost ambient pressure drying technique. With water wash and the following solvent exchange process for Na+ removal, this synthesis route has no ion exchange resin used and becomes more straightforward. In order to reduce the silica particle and pore sizes, different hydrolysis-condensation rate control agents including dimethylformamide (DMF), methyl-triethoxysilane (TMES), Glycerol and methyltrimethoxylsilane (MTMS) have been applied to modify the structural groups of silica network. Results show that MTMS is the most effective control agent and the optimized MTMS/silica sol volume ratio has been found at 1% by testing the specific surface area of the aerogel. In addition, the effects of chlorotrimethylsilane (TMCS) amount and the calcining temperature on the physicochemical properties of the aerogel have been also investigated. When the TMCS/silica sol volume ratio is 0.4, Thermogravimetric and Differential Scanning Calorimetry analysis (TG/DSC) measurement shows that there is an apprent exothermic peak at calcining temperture of 420 degrees C, caused by the transformation of Si-CH3 group to Si-OH group. X-ray photoelectric spectroscopy (XPS) results show that the percentages of Si-C(-H) bonds with binding energy of 102.4 eV have decreased from 25.5% to 7.2% after 420 degrees C calcining. The contact angle of the as-dried aerogel is as high as 154 and dramatically decreases to ca. 109 degrees after calcining at 450 degrees C. The pore volume and BET specific surface area both increase first and then decrease with the increase of calcining temperature, and the pore volume reaches the maxmium of 1.45 cm(3)/g at 400 degrees C and it confirms Si-CH3 group release. This study offers a new facile route to the synthesis of silica aerogel and presents a promising way of the cost-effective large-scale manufacturing.

Rapid synthesis of ambient pressure dried tetraethoxysilane based silica aerogels

Preparation and Heat Treatment of Titania Aerogels by Ambient Pressure Drying

Synthesis and characterization of silica aerogels by a novel fast ambient pressure drying process

Rapid synthesis of ambient pressure dried monolithic silica aerogels using water as the only solvent

Preparation of Methyltrimethoxysilane Derived Silica Aerogel Films via Ambient Pressure Drying

Production of low-density sodium silicate-based hydrophobic silica aerogel beads by a novel fast gelation process and ambient pressure drying process

Synthesis and characterization of low density and hydrophobic silica aerogels dried at ambient pressure using sodium silicate precursor

Preparation of Silica Aerogels Via Ambient Pressure Drying

Performance regulation of silica aerogel powder synthesized by a two-step Sol-gel process with a fast ambient pressure drying route

Convenient and rapid preparation of aerogels dried at ambient pressure

Synthesis and Characterization of Silica Aerogel and Its Composite Materials

In-situ acid catalysis strategy to achieve rapid ambient pressure drying preparation of aerogels

Rapid synthesis of sodium silicate based hydrophobic silica aerogel granules with large surface area

Effects of Surfactants on the Synthesis of Silica Aerogels Prepared by Ambient Pressure Drying

Low thermalconductive, transparent and hydrophobic ambient pressure dried silica aerogels with various preparation conditions using sodium silicate solutions

Synthesis and Effect of DCCA on the Ambient Pressure Dried, TEOS-Based Silica Aerogel

Synthesis of Hydrophobic Silica Aerogels via Ambient Pressure Drying

Silica aerogels formed from soluble silicates and methyl trimethoxysilane (MTMS) using CO2 gas as a gelation agent

Influence of Hydrolysis Time on Properties of SiO2 Aerogels Prepared by Ambient Pressure Drying

Preparation of ambient pressure dried MTMS/TEOS co-precursor silica aerogel by adjusting NH 4 OH concentration

High Compression Strength and Thermal Insulation Silica Aerogel Monolith with Scaffold of a Cyclic Olefin Siloxane Co-Oligomer Via Ambient Pressure Drying