Abstract:The process of reaction of silicon carbide ceramics derived from microporous carbon was investigated. The reaction mechanism was also analyzed. The ultimate microstructure of SiC ceramics are affected by the mass ratio of C to Si and infiltration time. Composite materials, which consist of SIC, Si and a small fraction of unreacted C, are obtained when the mass ratio of C to Si Is higher whereas partial infiltration Occurs when the mass ratio of C to Si is lower. Composite materials demonstrates many uniformly distributed strip-shaped SiC grains in certain region at transitional stage of reaction, and shows irregular SIC grains and an obvious bimodal distribution of grain size at terminal stage of reaction. The process of silicon-carbon reaction can be described as follows, melted Si ascends via capillary of micropore carbon and reacts with contacted carbon forming SiC. Size difference of pore and carbon wall induces difference of the infiltration deep of melted Si within micropore carbon and thicknesses of the dissolved carbon layer, respectively. As a result, sortie carbon particles are embedded in Sic grain an(l pore channel system is restructured. New pore channel with bigger pore size are formed, which accelerates Infiltration rate of melted Si. Then the unreacted carbons embedded in Sic grain are firstly diffuse through the SIC layer and dissolved in the Si melt, and then deposits on the first SIC formed. Finally, liquid epitaxial growth of SIC causes coalescence of SIC grains and envelopment of some Si in Sic grains, resulting in change of microstructure of SiC ceramics.

The Formation and Crystal Structure of Silicon Carbide

Silicon carbide: from amorphous to crystalline material

The structure of chemical vapor deposited silicon carbide

Phase formation of cubic silicon carbide from reactive silicon–carbon multilayers

Crystallization Behavior of Amorphous Si2bc3n Ceramic Monolith Subjected to High Pressure

Crystallisation mechanism of amorphous silicon carbide

High-Temperature Raman Spectroscopy of Nano-Crystalline Carbon in Silicon Oxycarbide

Low-temperature formation of nanocrystalline β-SiC with high surface area and mesoporosity via reaction of mesoporous carbon and silicon powder

Formation and Characterization of Si5C3 Type Silicon Carbide by Carbon Ion Implantation with a MEVVA Ion Source

Formation of carbon vacancy in 4H silicon carbide during high-temperature processing

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

XTEM and IR Absorption Analysis of Silicon Carbide Prepared by High Temperature Carbon Implantation in Silicon

Chemical Reactions in the Co–Si–C System

Crystalline Silicon Carbide Nanoparticles Encapsulated in Branched Wavelike Carbon Nanotubes: Synthesis and Optical Properties

A Simple Route to Nanocrystalline Silicon Carbide

Hardness and Thermal Stability of Cubic Silicon Nitride

Low temperature synthesis and photoluminescence of cubic silicon carbide

Microstructure Evolution and Reaction Mechanism of Microporous Carbon Derived SiC Ceramic

A novel approach for the synthesis of 6H-SiC at a low temperature of 460°C

Silicon carbide hollow nanospheres, nanowires and coaxial nanowires

Polymer-derived SiC/B4C/C nanocomposites: Structural evolution and crystallization behavior