Abstract:Arrays of randomly oriented zinc oxide (ZnO) nanowires were fabricated on silicon wafers via a simple thermal evaporation method. During the fabrication, the temperature around the substrate was below 500°C. The products were analyzed by conventional means and determined to be single crystals of wurtzite-type ZnO that grew along the c-axis. These nanowires were 10–100nm in diameter and 10–100μm in length, suggesting a possible high field enhancement factor. The dependence of the field emission current on the anode–cathode voltage (I–V behavior) of the ZnO nanowire arrays was measured in a lab-built ultrahigh vacuum system with a base pressure of 10−7Pa. After surface cleaning by heat treatment, two characteristic electric fields, under which 10μA/cm2 and 1mA/cm2 current densities were extracted, were measured to be 4.0 and 4.7V/μm, respectively. As observed with a transparent anode, emission occurred uniformly over the whole sample surface. A 72h-long test on emission stability was performed under a constant voltage of 2.75kV. The current dropped occasionally to approximately 80% of the initial value during the test owing to the poor adherence of the nanowires to the substrate. These preliminary results have shown the perspective of, as well as a major drawback to, a ZnO nanowire array being developed into a cold electron source to be used in future electronic devices.

Efficient field emission from ZnO nanoneedle arrays

Precisely-controlled Fabrication of Single ZnO Nanoemitter Arrays and Their Possible Application in Low Energy Parallel Electron Beam Exposure.

Field Emission Properties of Well-Ordered Zno Nanoneedle Arrays

Stable, Self-Ballasting Field Emission from Zinc Oxide Nanowires Grown on an Array of Vertically Aligned Carbon Nanofibers

Field Emission from Aln Nanoneedle Arrays

Fabrication of Large-Area ZnO Nanowire Field Emitter Arrays by Thermal Oxidation for High-Current Application

Field Emission from Nonaligned Zinc Oxide Nanowires

ZnO Nanowire Field Emitter Arrays: Fabrication, Field Emission Mechanism and Applications

Optimizing the Field Emission Properties of ZnO Nanowire Arrays by Precisely Tuning the Population Density and Application in Large-Area Gated Field Emitter Arrays.

A template-free electrochemical deposition route to ZnO nanoneedle arrays and their optical and field emission properties

Field Emission Properties of Zinc Oxide Nanowires Fabricated by Thermal Evaporation

Effect of N 2 flux on the field emission properties of synthesized ZnO/ZrN core-shell nanostructures

Fabrication Of Zno Nanowire Field Emitter Arrays For Field Emission Display Application

Enhanced Field Emission Performance of ZnO Nanorods by Two Alternative Approaches

Field Emission Properties of ZnO Nanowire Array Directly Grown from Zinc Substrate

Enhanced Field Emission from Injector-Like ZnO Nanostructures with Minimized Screening Effect

Ultrahigh Field Emission Current Density from Nitrogen-Implanted ZnO Nanowires.

Highly Efficient Field Emission from Large-Scale and Uniform Monolayer Graphene Sheet Supported on Patterned ZnO Nanorod Arrays

Fabrication of ZnO Nanowires by Vapor-Phase Deposition and Their Field Emission Properties

Field Emission from Zinc Oxide Nanostructures and Its Degradation

2D planar field emission devices based on individual ZnO nanowires