A high resolution transmission electron microscope study of early stage precipitation on dislocation lines in Al-Zn-Mg

Robert M. Allen,John B. VanDer Sande,John B. Sande

DOI: https://doi.org/10.1007/bf02652248

1978-09-01

Metallurgical Transactions A

Abstract:The weak beam transmission electron microscopy technique was employed to study the early stages of precipitation on dislocation lines in Al-3.87 wt pct Zn-1.79 wt pct Mg. The heterogeneous precipitation sequence was found to follow the homogeneous sequence in this alloy. The interaction between the initial coherent precipitate particles and the strain fields of the catalyzing dislocations produced “gaps” of background intensity at precipitate locations along the otherwise continuous weak beam images of the dislocation lines. A simple model was developed to relate a distribution of measured weak beam gap lengths to a particle size distribution at a given aging treatment. In this manner the growth kinetics of the initial precipitate phase was observed; it was found that the precipitation followed the Cottrell-Bilbyt2/3law, suggesting that matrix dislocations may assist the growth of heterogeneous precipitates in a manner analogous to grain boundary “collector plates.” Weak beam microscopy was found to be superior to standard bright field microscopy for the current study. Particles too small to be visible in bright field were revealed in weak beam. Weak beam observations also indicated that the coherent precipitate particles were positioned asymmetrically about the dislocation cores.

English Else