Abstract:Age hardening at 160 degrees C was performed in an Al-6.0 wt.%Zn-2.3 wt.%Mg-I.8 wt.%Cu-0.1 wt.%Zr alloy. It was found that metastable phases played a very important role in controlling this behaviour. The alloy reached the 193 HV peak hardness aged for 6 h. Transmission electron microscopy was used to characterise the morphology of iy phases as main strengthening precipitates, and then the high-resolution transmission electron microscopy, combining with Transition Matrix calculation, was used to analysis the orientations and electron diffraction patterns of eta' precipitates. It was found that the eta' phases in four variants had only three different zone axis: [2 (4) over bar 23](eta'), [10 (1) over bar0] T and [(2) over tilde4 (2) over bar3](eta'), parallel to the [110](Al) direction of Al matrix when they were precipitated. By integrating the atomic coordinates, structure factors and double diffraction effect, a new diffraction patterns model under the [110](Al) zone axis was established, which was good in agreement with the experimental result. Simultaneously, Moire fringes analytical technique was also used to quantitatively verify the lattice parameters and orientation variants of eta' precipitates, and demonstrated that Moire fringes with about 0.7 nm spacing were the results of the interaction between the 0004(eta')/4000 (4) over bar (eta'), diffraction eta' of Ti' precipitates in variants 3/4 under the [10 (1) over bar0] y zone axis and the 1 (1) over bar (Al)/1 (1) over bar(1) over bar (Al) of Al matrix under the [110](Al) zone axis. Furthermore, the high-resolution transmission electron microscopy image simulation for Moire fringes of eta' precipitates in the Al matrix presented a good match with the experimental result. (C) 2014 Elsevier B.V. All rights reserved.

Transmission Electron Microscopy Investigation and Interpretation of the Morphology and Interfacial Structure of the ∊′-Mg54ag17precipitates in an Mg–Sn–Mn–Ag–Zn Alloy

Evolution of Precipitate and Precipitate/matrix Interface in Al-Zn-Mg-Cu(-Ag)alloys

Characterization and Interpretation of Interfacial Structure of the Mg2Sn Laths in an Mg–Sn–Mn–Ag–Zn Alloy

The morphology and crystallography of polygonal Mg2Sn precipitates in a Mg–Sn–Mn–Si alloy

Characterization and Interpretation on the New Crystallographic Features of a Twin-Related Ε′-Mg54ag17 Precipitates in an Mg–Sn–Mn–Ag–Zn Alloy

Precipitation in an Al-Zn-Mg-Cu alloy during isothermal aging: Atomic-scale HAADF-STEM investigation

Transmission Electron Microscopy Study of the Early-Stage Precipitates in Al-Mg-Si Alloys

Atomic-scale Characterization of the Precipitates in a Mg-Gd-Y-Zn-Mn Alloy Using Scanning Transmission Electron Microscopy

Characterization and Interpretation of the Morphology of a Mg2Sn Precipitate with Irrational Facets in a Mg–Sn–Mn Alloy

Interpretation of Precipitation Crystallography Ofmg(17)Al(12) in A Mg-Al Alloy in Terms of Singular Interfacial Structure

Interfacial Dislocation Induced Precipitation in a Mg−Gd−Zn−Zr Alloy

Crystallography of Mg2Sn Precipitates in Mg-Sn-Mn-Si Alloy

Co-segregation of Mg and Zn atoms at the planar η1-precipitate/Al matrix interface in an aged Al–Zn–Mg alloy

A transmission electron microscopy investigation of crystallography of τ-Mg32(Al, Zn)49 precipitates in a Mg–Zn–Al alloy

Zn Segregation at Precipitate/Matrix Interface in Mg-Sn-Zn Alloys

Precipitation Behaviour of Al–Zn–Mg–Cu Alloy and Diffraction Analysis from Η′ Precipitates in Four Variants

High-resolution electron microscopy observations of the interface structure of continuous precipitates in a Mg-Al alloy and interpretation with the O-lattice theory

Revisiting the precipitation mechanisms of Guinier-Preston zones, η′, and η precipitates in Al-Zn-Mg alloys

Atomic-scale Investigation of Precipitate Phases in QE22 Mg Alloy

HRTEM and HAADF-STEM Tomography Investigation of the Heterogeneously Formed S (al2cumg) Precipitates in Al–Cu–Mg Alloy

Aperiodic structures of rod-shaped precipitates in a Mg-Zn-Al alloy