Abstract:The polycrystalline IN713C produced via investment casting is one of the widely-used nickel-based superalloy in automotive and aerospace industries. This alloy, however, has an apparent inhomogeneous microstructure generated during casting and contains dendritic structure that gives rise to strain localisation during loading. Yet, the effect of dendrite structure, grain size and shape as well as crystallographic orientation, which directly influence fatigue property and deformation micromechanism in the components, is rarely studied. In the present study, IN713C cast bars are tailored with three different grain structures, i.e., transition, equiaxed and columnar, with substantial grain size variations. The produced bars were tested under strain controlled LCF (Low Cycle Fatigue) and stress controlled HCF (High Cycle Fatigue) conditions at 650 °C. The results showed that most of fatigue cracks initiated from casting porosities and fatigue life extended in the microstructure with a small grain size during both HCF and LCF loadings. It is also demonstrated that fatigue striations were mainly observed within dendrite areas during crack propagation, whereas the higher GND (Geometrically Necessary Dislocation) density were predominantly observed in the interdendrite areas. Here, we propose a concept of 'Crack Propagation Unit (CPU)' for better description of deformation mechanism at local scale during fatigue loading by combining fracture surface characteristic methodology and dislocation distribution analyses within the dendrite structural unit. Furthermore, this model to understand the deformation micromechanism can provide a new perspective on the interpretation of Hall-Petch relationship in casting materials that contain dendritic structure. This is further demonstrated via direct correlation of the high crack propagation resistance with the crack path divergence instead of the dislocation pile-up at the grain boundary or in-between the γ/ γ' channels. Moreover, by utilising serial sectioning method followed by layered EBSD scanning, quasi-3-D grain orientation mappings were obtained, and crystallographic texture information were directly correlated with the fracture surface observations. This allowed an investigation of the influence of orientation of individual grains and micro/macro texture on crack propagation rate. The critical stage of crack propagation in fatigue life and its correlations with microstructural features is established, offering potential practical applications by controlling the investment casting process parameters.

Measurement of Crystal Orientation around the Fatigue Crack in Iron Films Using EBSD Method

Microscopic Analysis by EBSD Method on Fatigue Crack Propagation Behaviour in Ultrafine-Grained Copper

Fracture Mode Identification of Low Alloy Steels and Cast Irons by Electron Back-Scattered Diffraction Misorientation Analysis

Crystal Orientation Effect on Fretting Fatigue Induced Geometrically Necessary Dislocation Distribution in Ni-based Single-Crystal Superalloys

Influence of the Crystalline Orientations on Microcrack Initiation in Low-Cycle Fatigue

Cyclic Stress Measurement in a Microscopic Region Using EBSD Analysis of Grown Grains Occurred in the Copper Foil

1216 Nano-Scale Strength Analysis by EBSD and AFM Hybrid Method in Ultrafine-Grained Copper Processed by ECAP

EBSD Analysis of Cyclic Load Effect on Final Misorientation Distribution of Post-Mortem Low Alloy Steel: A New Method for Fatigue Crack Tip Driving Force Prediction

Microscopic Observations of Fatigue Crack Initiation Process in 18-8 Austenitic Steel

In-situ Observations of the Effects of Orientation and Carbide on Low Cycle Fatigue Crack Propagation in a Single Crystal Superalloy

Identification of crack orientation in electrically conductive materials using eddy current testing powered by rotational directive filter

Fatigue life assessment of nickel-based single crystals considering equivalent initial flaw size model and anisotropy

In-situ fatigue behavior study of a nickel-based single-crystal superalloy with different orientations

The effect of crystal orientation on fretting fatigue crack formation in Ni-based single-crystal superalloys: In-situ SEM observation and crystal plasticity finite element simulation

The Effects of Grain Size, Dendritic Structure and Crystallographic Orientation on Fatigue Crack Propagation in IN713C Nickel-Based Superalloy

Prediction of Static Recrystallization Nucleation Sites in Tensile Deformed Single Crystal Pure Iron through a Combination of In-Situ EBSD and CP-FEM

Crystallographic orientation assessment by electron backscattered diffraction

Effect of crack closure on quantitative ECT inspection of closed fatigue cracks

Integrating atomistics and experiments in gaining deeper insights into fatigue crack propagation in silver

Application of the EBSD technique to describe the initiation and growth behaviour of microstructurally short fatigue cracks in a duplex steel

Application of Electron Backscatter Diffraction in Facet Crystalline Orientation Study of Al-Cu-Fe Alloy