Abstract:In this study, a method for detecting defects in carbon fiber‐reinforced polymers (CFRPs) using a new probe to measure eddy current loss is proposed. The comparison of eddy current loss among different types of CFRPs is presented, scanning imaging results of orthogonally woven CFRP sample further demonstrate the detection performance, and the fiber orientation of CFRPs is characterized. Eddy current testing (ECT) is a widely used technique for detecting defects in carbon fiber‐reinforced polymers (CFRPs) at high frequencies. However, designing high‐frequency systems can be challenging, and high noise levels can be problematic. To address these issues, non‐destructive testing (NDT) methods that can detect CFRP defects at lower frequencies must be explored. In this study, a novel NDT method for detecting defects in CFRP at low frequencies was proposed. This method is an alternative to pulsed eddy current thermography and can achieve similar detection and imaging results at low frequencies. Furthermore, the developed method has a simpler structure and is easier to implement. This method uses the eddy current loss to characterize the thermal power of the eddy current in CFRP. A new probe was used to detect the eddy current loss to inspect the CFRP. The effectiveness of the proposed method was experimentally verified using different types of CFRP samples based on the C‐scan technology. The scanned images demonstrate that the developed method can provide appropriate detection results up to a frequency of 750 kHz. Furthermore, rotation experiments were performed to detect the fiber direction; the proposed method successfully detected the fiber direction up to 750 kHz. Thus, the proposed method can improve the detection of defects and enhance the longevity of CFRP components. Future work will focus on enhancing the sensitivity of this method at even lower frequencies.

Identification of crack orientation in electrically conductive materials using eddy current testing powered by rotational directive filter

Reconstruction of Cracks in a Carbon Fiber-Reinforced Polymer Laminate Plate from Signals of Eddy Current Testing

GMR effect based crack ECT for nonferromagnetic metal material

RCF crack direction assessment in moving ferromagnetic material by DC electromagnetic NDT technique

Non-destructive testing for carbon-fiber-reinforced plastic (CFRP) using a novel eddy current probe

Differential ECT Probe Design and Investigation for Detection of Rolling Contact Fatigue Cracks With Different Orientations

Noncontact Visualization of Multiscale Defects in CFRP Composites using Eddy Current Testing with T-R Probe

A new probe‐based electromagnetic non‐destructive testing method for carbon fiber‐reinforced polymers utilizing eddy current loss measurements

A Nondestructive Strategy for the Distinction of Natural Fatigue and Stress Corrosion Cracks Based on Signals from Eddy Current Testing

Detectability Evaluation of Eddy Current Testing Probes for Inspection of Defects in Carbon Fiber Reinforced Polymer Laminates

Eddy current non-destructive evaluation of manufacturing flaws and operational damage in CFRP composites

Non-Destructive Evaluation of In-Plane Waviness in Carbon Fiber Laminates Using Eddy Current Testing

A Fast Forward Simulation Scheme for Eddy Current Testing of Crack in a Structure of Carbon Fiber Reinforced Polymer Laminate

Nondestructive Evaluation of Nylon/carbon-Fiber Additively Manufactured Components Using Rotational Eddy Current Testing

Fast Simulation of ECT Signal Due to a Conductive Crack of Arbitrary Width

A New Differential Eddy Current Testing Sensor Used for Detecting Crack Extension Direction

Fatigue Crack Length Sizing Using a Novel Flexible Eddy Current Sensor Array

Non-Destructive Testing of Carbon Fiber-Reinforced Plastics (CFRPs) Using a Resonant Eddy Current Sensor

Characterization of Rolling Contact Fatigue Cracks in Rails by Eddy Current Pulsed Thermography

Reconstruction of Cracks with Physical Closure from Signals of Eddy Current Testing

Quantitative Mapping of Depth Profile of Fatigue Cracks Using Eddy Current Pulsed Thermography Assisted by PCA and 2D Wavelet Transformation