Abstract:A high cycle fatigue life prediction model based on continuum damage mechanics, crystal plas-ticity and critical distance theory is developed. A novel damage evolution law for anisotropic Ni-based single crystal materials built on continuum damage mechanics is proposed. The crystal plasticity framework was introduced to take into account the particular characteristics of high cycle fatigue. The critical distance theory was innovatively applied to the structure of film cooling holes to predict the lifetime for materials under a multiaxial stress state. High cycle fatigue tests considering drilling technology, stress ratio and creep time were performed using Ni-based single crystal superalloy plates with film cooling holes. The constitutive equations were implemented into a finite element framework to simulate the high cycle fatigue properties of Ni-based single crystal superalloys, and the results of numerical calculations were compared with experimental observations. It was demonstrated that the constitutive formulations proposed in the present study can be used to model the mechanical behavior of Ni-based single crystal superalloys under a multiaxial stress state. The life prediction errors are found to be within the factor-of-three scatter band. The fatigue life of the specimen with ultrafast laser drilled film cooling holes is larger than that with electrostream machined film cooling holes under the same test conditions. The fatigue strength of the specimen with film cooling holes at a stress ratio R = 0.95 is higher than that at a stress ratio R =-1. The life of the specimen with film cooling holes is found to decrease with increasing creep time before high cycle fatigue. The gamma/gamma'-microstructure evolution in the speci-mens with film cooling holes is related to the kinetics of the stress redistribution during the fa-tigue process. A minimum stress level is essential for rafting to occur. The damage distribution for the plate model is in line with the crack initiation location and propagation region of the specimen.

Fatigue life assessment of nickel-based single crystals considering equivalent initial flaw size model and anisotropy

High Cycle Fatigue Life Prediction Model Based on Crystal Plasticity and Continuum Damage Mechanics for Ni-based Single Crystal Superalloys under a Multiaxial Stress State

Fatigue Fracture Mechanism and Life Assessment for Irregular Film Cooling Hole Structures in Ni-based Single Crystal Turbine Blades

The EIFS-based fatigue life prediction approach of nickel-based single crystals with film cooling holes at elevated temperature

Fatigue Life Prediction of Film-cooling Hole Specimens with Initial Damage

Fatigue Life Estimation of Nickel-Based Single Crystal Superalloy with Different Inclined Film Cooling Holes: Initial Damage Quantification and Coupling of Damage-Fracture Mechanics Models

Investigation on High Temperature Fatigue-Oxidation Behavior of Ni-based Single Crystal with Film Cooling Holes Considering Arrangement Effect

Effects of Roundness of Laser Formed Film Cooling Holes on Fatigue Life of Nickel Based Single Crystal

Evaluation of different drilling quality and fatigue life prediction of nickel-based superalloy using equivalent initial flaw size

Effect Mechanism and Equivalent Model of Surface Roughness on Fatigue Behavior of Nickel-Based Single Crystal Superalloy

Fatigue Crack Initiation and Propagation Behavior of Nickel-Based Single Crystal DD6 under Different Drilling Processes

Evaluation method of equivalent initial flaw size and fatigue life prediction of nickel-based single crystal superalloy

Vibration Fatigue of Film Cooling Hole Structure of Ni-based Single Crystal Turbine Blade: Failure Behavior and Life Prediction

Fatigue Life Prediction Based On Crack Closure And Equivalent Initial Flaw Size

Quantitative Study of High-Frequency Fatigue Hole-Edge Stresses in Nickel-Based Single-Crystal Superalloy

Low Cycle Fatigue Behavior and Crack Initiation Mechanism of Ni-based Single Crystal Curved Thin-Walled Blade Simulator Specimen with Film Cooling Holes

A Low-Cycle Fatigue Life Model of Nickel-Based Single Crystal Superalloys under Multiaxial Stress State

Thermodynamics-based Method Considering Orientation and Notch Effect to Predict the High Cycle Fatigue Life of a Nickel-Based Single Crystal Superalloy

A Crystallographic Model for the Orientation Dependence of Low Cyclic Fatigue Property of a Nickel-Base Single Crystal Superalloy

A safe fracture fatigue life prediction based on equivalent initial flaw size

Calibrated the Direct Current Potential Drop Method for Fatigue Crack Propagation Testing of Nickel-Based Superalloy with Film Cooling Hole