Abstract:A high-temperature, high-cycle fatigue test was conducted on a nickel-based single-crystal superalloy with a pore structure. Optical and scanning electron microscopy were utilized to examine the crack propagation paths and fatigue fracture surfaces at the macro and micro scales. The analysis of crack initiation and propagation related to the pore structure facilitated the development of a crack shape factor reflecting these distinct fracture behaviors. Predictions about the high-cycle fatigue stress experienced by the specimen were made, accompanied by an error analysis, providing critical insights for precise stress calculations and structural optimization in engine blade design. The results reveal that high-cycle fatigue cracks originate from corner cracks at pore edges, with the initial propagation displaying smooth crystallographic plane features. Subsequent stages show clear fatigue arc patterns in the propagation zones. The fracture surface exhibits the significant layering of oxide layers, primarily composed of NiO, with traces of CoO displaying columnar growth. AL2O3 is predominantly found at the interfaces between the matrix and oxide layers. Short and straight dislocations near the oxide layers and within the matrix suggest that dislocation multiplication and planar slip dominate the slip mechanisms in this alloy. The orientation of the fracture surface is mainly perpendicular to the load direction, with minor inclined facets in localized areas. Correlations were established between the plastic zone dimensions at the crack tips and the corresponding fatigue stresses. Without grain boundaries in single-crystal alloys, these dimensions are easily derived as parameters for fatigue stress analysis. The selected crack shape factor, "elliptical corner crack at pore edges", captures the initiation and propagation traits relevant to porous structures. Subsequent calculations, accounting for the impact of oxide layers on stress assessments, indicated an error ratio ranging from 1.00 to 1.21 compared to nominal stress values.

Evaluation of different drilling quality and fatigue life prediction of nickel-based superalloy using equivalent initial flaw size

The EIFS-based fatigue life prediction approach of nickel-based single crystals with film cooling holes at elevated temperature

A Study of Fatigue Mesoscopic Elasto-Plastic Properties of a Nickel-Base Superalloy by Instrumented Microindentation Measurements

Fatigue life assessment of nickel-based single crystals considering equivalent initial flaw size model and anisotropy

Investigation of fatigue mesoscopic mechanical properties of a nickel-based superalloy by instrumented microindentation measurements

Fatigue Life Prediction of Film-cooling Hole Specimens with Initial Damage

Evaluation method of equivalent initial flaw size and fatigue life prediction of nickel-based single crystal superalloy

Quantitative Study of High-Frequency Fatigue Hole-Edge Stresses in Nickel-Based Single-Crystal Superalloy

A safe fracture fatigue life prediction based on equivalent initial flaw size

The whole fatigue crack propagation life prediction of Ni-based single crystal super-alloy specimen with single hole based on EIFS and ‘Fish-eye’ theory

Prediction of Fatigue Crack Damage Using In-Situ Scanning Electron Microscopy and Machine Learning

High-Cycle Fatigue Fracture Behavior and Stress Prediction of Ni-Based Single-Crystal Superalloy with Film Cooling Hole Drilled Using Femtosecond Laser

Thermomechanical fatigue and life prediction method of a precision cast superalloy with electrical discharge machining drilled holes

Fatigue Life of Ni-Based Single Crystal Super-Alloy Specimen with Single Hole

Crack initiation mechanisms and life prediction of GH4169 superalloy in the high cycle and very high cycle fatigue regime

Dislocation-based crystal plasticity modelling of a nickel-based superalloy under dwell-fatigue: From life prediction to residual life assessment

Experimental and simulated investigations of low cycle fatigue behavior in a nickel-based superalloy with different volume fractions of δ phase

Creep-fatigue life prediction in nickel-based superalloy GH4169 based on microstructural damage quantification with the help of electron backscatter diffraction

A crystal plasticity-based approach for creep-fatigue life prediction and damage evaluation in a nickel-based superalloy

A topologized resolved shear stress method for the life prediction of nickel-base single crystal superalloys

A novel very-high-cycle-fatigue life prediction model with interior microstructure induced cracking behavior of Inconel-713C superalloy at 25 °C, 750 °C and 1000 °C