Abstract:The in-situ synthesized mullite bonded SiC ceramics for solar thermal tower plant were prepared from Silicon carbide (SiC), manufactured aluminum hydroxide (Al(OH)3) and Suzhou kaolin via semi-dry pressing and pressureless firing. The results indicate that sample B3 (designed mullite content 15 wt%) fired at 1 400 °C exhibited optimal performance with a bending strength of 97.41 MPa. Sample B3 can withstand 30-cycles thermal shock without cracking (wind cooling from 1 100 °C to room temperature), and the bending strength after thermal shock decreased by 17.92%. When the service temperature is 600 °C, the thermal diffusivity, specific heat capacity, thermal conductivity and heat capacity are 6.48×10−2 cm2·s−1, 0.69 kJ·kg−1· K−1, 9.62 W·m−1·K−1 and 977.76 kJ·kg−1, respectively. The XRD and SEM results show that SiC, mullite, α-quartz, and tridymite are connected closely, which gives the material a good bending strength. After 30-time thermal shock cycles, the structure of samples becomes loose. SiC grains are intersectingly arranged with rodshape mullite, exhibiting a favorable thermal shock resistance. The addition of Al(OH)3 and Suzhou kaolin can accelerate the synthesis of mullite, thus to reduce the firing temperature effectively. The volume effect of tridymite is relatively small, improving the thermal shock resistance of materials. A higher designed mullite content yields a lower loss rate of bending strength. The mullite content should not be more than 15 wt% or else the bending strength would be diminished.

Reaction Behavior of High-purity Mullite Container with Melted Solar Salts

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

High purity mullite ceramics by reaction sintering

Reaction Bonding of Porous Mullite Ceramics

Mullite formation from reaction sintering of ZrSiO4/α-Al2O3 mixtures

Reaction mechanisms and properties of in situ porous Al2O3-ZrO2-mullite composites

Fabrication and characterization of porous mullite ceramics with ultra-low shrinkage and high porosity via sol-gel and solid state reaction methods

Preparation and Characterization of Mullite Whiskers from Different Silica Sources via Molten Salt Reaction

REACTION SINTERING OF Al2O3/SiC COMPOSITE IN AIR

Preparation and properties of porous mullite-based ceramics fabricated by solid state reaction

Properties of Mullite Sol Bonded with High Aluminum Refractories

Reaction sintering of ZrSiO4/α-Al2O3 mixed powders with Y2O3 addition

Preparation of mullite ceramics with equiaxial grains from powders synthesized by the sol-gel method

Preparation of Dense Mullite Ceramics through Gelcasting of Alumina Slurry Dispersed in Silica Sol

Thermal decomposition and reaction sintering for synthesis of mullite-zirconia composite using kaolin, γ-alumina and zirconia

Preparation of Mullite Monoliths with Well-Defined Macropores and Mesostructured Skeletons Via the Sol–gel Process Accompanied by Phase Separation

IN SITU REACTION SINTERING AND CHARACTERIZATION OF MULLITE-CORDIERITE COMPOSITES

Molten salt synthesis of mullite whiskers from various alumina precursors

Preparation and characterization of mullite-silicon carbide heat absorbing ceramics for solar thermal tower plant

Molten Salt Synthesis of Mullite Whiskers from Silicon Carbide Precursor

High-Gravity Combustion Synthesis of Al2tio5/Mullite Ceramic Composites