Abstract:The properties of silica aerogels, and the ability to prepare them by ambient pressure drying, hinge on their chemical surface modification. Until now, quantitative analysis of the surface chemistry has not been possible by state-of-the-art analytical methods. Here, we determine the surface chemistry of six archetypal, ambient pressure dried, hydrophobic silica aerogels and open-porous foams with quantitative 1H, 13C, and 29Si and 1H–29Si heteronuclear solid-state NMR spectroscopy. The quality of the external calibration, the validation by elemental analysis, and the consistency among the 1H, 13C, and 29Si MAS NMR data enable us to robustly quantify the surface chemistry of these classical silica materials. Four aerogels were derived from tetraethoxysilane (TEOS), polyethoxydisiloxane (PEDS), or waterglass precursors and hydrophobized with trimethylsilyl (TMS) groups through immersion in hexamethyldisilazane (HMDZ) in heptane, trimethylchlorosilane (TMCS) in heptane, or hexamethyldisiloxane (HMDSO) in ethanol. The resulting aerogels display remarkably similar chemistries despite their very different precursors (alkoxides, waterglass), hydrophobization agents (HMDZ, TMCS, HMDSO), and gelation and hydrophobization solvents (water, ethanol, heptane). The TMS content is nearly the same (22–27 wt %), the ethoxy content is low (<4 wt %), and the silica speciation displays a narrow range for all four aerogels. The 1H–29Si heteronuclear correlation spectra provide unambiguous evidence for the grafting of the TMS groups on the silica surfaces. Remarkably, the NMR data enable the prediction of the silica particle size to within 1 to 2 nm of that derived by TEM analysis. Two additional, inherently hydrophobic, ambient pressure dried, open-porous silica foams were synthesized from methyltrimethoxysilane (MTMS) and from a MTMS–dimethyldimethoxysilane (DMDMS) mixture. The reduction in the number of bridging oxygens per Si atom, from 3.76 to 3.90 for TEOS, PEDS, or waterglass based aerogels, to 2.86 for the MTMS based open-porous foam, and to 2.48 for the MTMS–DMDMS derived open-porous foam, results in a brittle-to-superflexible transition. Our results highlight the importance of the chemical treatment of the wet gels (hydrophobization and solvent exchange) on the final surface chemistry of silica aerogels.

Synthesis of sodium silicate-based hydrophilic silica aerogel beads with superior properties: Effect of heat-treatment

Synthesis and characterization of micrometer-sized silica aerogel nanoporous beads

Production of low-density sodium silicate-based hydrophobic silica aerogel beads by a novel fast gelation process and ambient pressure drying process

Preparation and Heat Treatment of Titania Aerogels by Ambient Pressure Drying

Surface chemistry, skeleton structure and thermal safety of methylsilyl modified silica aerogels by heat treatment in an argon atmosphere

Preparation of Methyltrimethoxysilane Derived Silica Aerogel Films via Ambient Pressure Drying

Synthesis of hydrophilic and hydrophobic xerogels with superior properties using sodium silicate

Regulating the hydrophobicity and pore structure of silica aerogel for thermal insulation under humid and high temperature conditions

Improvement of the Thermal Insulation Performance of Silica Aerogel by Proper Heat Treatment: Microporous Structures Changes and Pyrolysis Mechanism

Synthesis of Al2O3-SiO2 aerogels with low thermal conductivity and high strength by methyltriethoxysilane as a silica precursor

Surface Chemistry of Hydrophobic Silica Aerogels

Synthesis of high specific surface area silica aerogel from rice husk ash via ambient pressure drying

Synthesis of a novel Al 2 O 3 –SiO 2 composite aerogel with high specific surface area at elevated temperatures using inexpensive inorganic salt of aluminum

Low thermalconductive, transparent and hydrophobic ambient pressure dried silica aerogels with various preparation conditions using sodium silicate solutions

Synthesis and Textural Evolution of Mesoporous Si3N4 Aerogel with High Specific Surface Area and Excellent Thermal Insulation Property Via the Urea Assisted Sol-Gel Technique

Effect of different trimethyl silylating agents on the hydrophobic and physical properties of silica aerogels

Alumina-Doped Silica Aerogels for High-Temperature Thermal Insulation

Superhydrophobic silica aerogel powders with simultaneous surface modification, solvent exchange and sodium ion removal from hydrogels

Silica aerogels formed from soluble silicates and methyl trimethoxysilane (MTMS) using CO2 gas as a gelation agent

Effects of Surfactants on the Synthesis of Silica Aerogels Prepared by Ambient Pressure Drying

Rapid synthesis of sodium silicate based hydrophobic silica aerogel granules with large surface area