Abstract:The properties of silica aerogels, and the ability to prepare them by ambient pressure drying, hinge on their chemical surface modification. Until now, quantitative analysis of the surface chemistry has not been possible by state-of-the-art analytical methods. Here, we determine the surface chemistry of six archetypal, ambient pressure dried, hydrophobic silica aerogels and open-porous foams with quantitative 1H, 13C, and 29Si and 1H–29Si heteronuclear solid-state NMR spectroscopy. The quality of the external calibration, the validation by elemental analysis, and the consistency among the 1H, 13C, and 29Si MAS NMR data enable us to robustly quantify the surface chemistry of these classical silica materials. Four aerogels were derived from tetraethoxysilane (TEOS), polyethoxydisiloxane (PEDS), or waterglass precursors and hydrophobized with trimethylsilyl (TMS) groups through immersion in hexamethyldisilazane (HMDZ) in heptane, trimethylchlorosilane (TMCS) in heptane, or hexamethyldisiloxane (HMDSO) in ethanol. The resulting aerogels display remarkably similar chemistries despite their very different precursors (alkoxides, waterglass), hydrophobization agents (HMDZ, TMCS, HMDSO), and gelation and hydrophobization solvents (water, ethanol, heptane). The TMS content is nearly the same (22–27 wt %), the ethoxy content is low (<4 wt %), and the silica speciation displays a narrow range for all four aerogels. The 1H–29Si heteronuclear correlation spectra provide unambiguous evidence for the grafting of the TMS groups on the silica surfaces. Remarkably, the NMR data enable the prediction of the silica particle size to within 1 to 2 nm of that derived by TEM analysis. Two additional, inherently hydrophobic, ambient pressure dried, open-porous silica foams were synthesized from methyltrimethoxysilane (MTMS) and from a MTMS–dimethyldimethoxysilane (DMDMS) mixture. The reduction in the number of bridging oxygens per Si atom, from 3.76 to 3.90 for TEOS, PEDS, or waterglass based aerogels, to 2.86 for the MTMS based open-porous foam, and to 2.48 for the MTMS–DMDMS derived open-porous foam, results in a brittle-to-superflexible transition. Our results highlight the importance of the chemical treatment of the wet gels (hydrophobization and solvent exchange) on the final surface chemistry of silica aerogels.

Surface chemistry, skeleton structure and thermal safety of methylsilyl modified silica aerogels by heat treatment in an argon atmosphere

Experimental Investigation of the Combustion Characteristics and Thermal Hazards of Methylsilyl-Modified Silica Aerogels

Regulating the hydrophobicity and pore structure of silica aerogel for thermal insulation under humid and high temperature conditions

Improvement of the Thermal Insulation Performance of Silica Aerogel by Proper Heat Treatment: Microporous Structures Changes and Pyrolysis Mechanism

Preparation of Methyltrimethoxysilane Derived Silica Aerogel Films via Ambient Pressure Drying

Facile Synthesis of Flexible and Hydrophobic Polymethylsilsesquioxane Based Silica Aerogel Via the Co-Precursor Method and Ambient Pressure Drying Technique

Synthesis of sodium silicate-based hydrophilic silica aerogel beads with superior properties: Effect of heat-treatment

Surface Chemistry of Hydrophobic Silica Aerogels

Study on Silica Aerogel Modified by Trimethylchlorosilane

In-Situ Synthesis of Layered Double Hydroxide/Silica Aerogel Composite and Its Thermal Safety Characteristics

Synthesis of Al2O3-SiO2 aerogels with low thermal conductivity and high strength by methyltriethoxysilane as a silica precursor

Thermal and hydrothermal stability of amino-functionalized SBA-16 and promotion of hydrophobicity by silylation

Reducing the thermal hazard of hydrophobic silica aerogels by using dimethyldichlorosilane as modifier

Enhancing thermal safety of hydrophobic silica aerogels by incorporating sodium dodecyl sulfate intercalated layered double hydroxides

Preparation of High-Temperature Resistant Aerogels by Incorporating Aluminum Sol into Composite Silica Sources Using Ambient Pressure Drying

Synthesis, structures and properties of hydrophobic Alkyltrimethoxysilane-Polyvinyltrimethoxysilane hybrid aerogels with different alkyl chain lengths

Preparation of high-strength silica aerogels by two-step surface modification via ambient pressure drying

Flexible, high-temperature-resistant silica-polymer aerogel hybrids by templating polymethylsilsesquioxane microstructure with trace polyimide

Synthesis and Textural Evolution of Mesoporous Si3N4 Aerogel with High Specific Surface Area and Excellent Thermal Insulation Property Via the Urea Assisted Sol-Gel Technique

Silica aerogels formed from soluble silicates and methyl trimethoxysilane (MTMS) using CO2 gas as a gelation agent

Alumina-Doped Silica Aerogels for High-Temperature Thermal Insulation