High-temperature degradation of the in-situ laser-glazed plasma sprayed LaMgAl11O19 thermal barrier coating exposed to Ca-Mg-Al-silicate deposits

Yiwei Sun,Hengkai Wu,Hongxu Zhao,Xiaolong Chen,Chaoqian Guo,Junbin Sun,Xueqiang Cao,Chunming Deng,Wei Li

DOI: https://doi.org/10.1016/j.corsci.2020.108934

IF: 7.72

2020-11-01

Corrosion Science

Abstract:<p>High-temperature degradation of the plasma sprayed LaMA coating before and after in-situ laser-glazing under CMAS attacks at 1350 °C for 1 h, 12 h and 48 h was comparatively investigated. Results indicate that a dense laser-glazed top layer was successfully created in-situ for a ~1 mm thick LaMA coating. It behaved as a sealing layer and reservoir of Al³⁺, Mg²⁺ and La³⁺. Melted CMAS penetration was accordingly effectively arrested accompanied by crystallizations of the CaAl₂Si₂O₈ anorthite, MgAl₂O₄ spinel and Ca₂La₈(SiO₄)₆O₂ apatite. CMAS-induced degradation mainly occurred near the surface of the laser-glazed dense LaMA top layer. While significant penetration of the melted CMAS along the entire thickness occurred to the as-sprayed LaMA coating without laser-glazing treatments after 48 h degradation. Ca₂La₈(SiO₄)₆O₂ apatite phase did not crystallize for the as-sprayed LaMA due to the much reduced local La³⁺ concentration in melted CMAS resulted from its porous microstructure. Effects of laser-glazing on the CMAS-induced degradation of the plasma sprayed LaMA was carefully analyzed and discussed in terms of the coating's chemical composition, microstructure and surface physical chemistry characteristics base on XRD, SEM/EDS and TEM results.</p>

materials science, multidisciplinary,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the high - temperature degradation problem of LaMgAl\(_{11}\)O\(_{19}\) (LaMA) thermal barrier coatings treated by laser in - situ cladding under the attack of Ca - Mg - Al - silicate (CMAS) deposits at high - temperature conditions. Specifically, the research focuses on how to form a dense barrier layer on the surface of LaMA coatings through laser in - situ cladding technology, so as to improve its resistance to CMAS erosion and thus extend its service life in high - temperature environments. By comparing and analyzing the degradation of LaMA coatings without laser treatment and with laser treatment after interacting with CMAS at 1350°C for 1 hour, 12 hours and 48 hours, the paper explores the effectiveness of laser treatment in improving the anti - CMAS erosion performance of LaMA coatings.