Enhanced structural stability of yttria‐stabilized zirconia–LaMgAl11O19 dual ceramic coating by an α‐Al2O3 layer

Haotian Tao,Tianxin Liu,Sirui Yang,Suying Hu,Rui Ma,Zhiwen Xie

DOI: https://doi.org/10.1111/ijac.14748

2024-04-01

International Journal of Applied Ceramic Technology

Abstract:The coating without AlY layer showed poor structural stability and unsatisfactory oxidation resistance at 1000°C. LaMA layer experienced significant recrystallization reaction, leading to fast TGO growth and severe structural fracture. However, this coating with AlY layer showed stable structure and good oxidation resistance. The AlY player was oxidized at 1000°C resulting in the formation of dense α‐Al2O3. The α‐Al2O3 barrier layer suppressed rapid TGO growth and structural fracture. To prolong the service life and structural stability of CoCrNiAlY–yttria stabilized zirconia–LaMgAl11O19 (LaMA) dual ceramic coating during high temperature exposure, an AlY plating layer was deposited on top LaMA. Results revealed that this coating without AlY plating layer showed a rapid mass increase from 6.62 mg/cm2 at 20 h to 10.63 mg/cm2 at 80 h, but also suffered from a fast TGO growth and severe elemental diffusion, resulting in an exacerbating interface fracture of the coating. However, AlY plating layer was first oxidized, and Y2O3 induced the formation of a dense α‐Al2O3 reaction layer on the top LaMA layer, which greatly prevented the internal penetration of O2. This coating with AlY plating layer showed a relatively stable structure, a very slow TGO growth, and a slight mass increase trend from 8.19 mg/cm2 at 20 h to 8.73 mg/cm2 at 80 h. Potential oxidation damage mechanisms of the coatings with or without AlY plating layer were comprehensively clarified.

materials science, ceramics