Abstract:Cr–Al-based oxynitride materials have attracted significant attention as hard protective coatings for decades. However, knowledge of the influence of the constituents on oxidation behavior is limited. Here, Cr–Al–O–N coatings with various Cr/Al ratios prepared using cathodic arc evaporation were studied with respect to their microstructure, mechanical properties, and oxidation behavior. With a decrease in the Cr/Al ratio, the coatings yielded a phase evolution from face-centered cubic CrN to rock salt-type cubic (Cr, Al) 2 O 3 to a wurtzite-type hexagonal AlN structure. The cubic structured coatings showed a comparable indentation hardness, much higher than that of the Cr-free Al–O–N coating with a wurtzite structure. Thermogravimetric together with differential scanning calorimetric (TG-DSC) analysis revealed that the ternary Cr–O–N and Al–O–N coatings were more susceptible to oxidation than the quaternary Cr–Al–O–N coatings. Moreover, isothermal oxidation experiments indicated that the addition of 66 at.% Al within the metallic species gives rise to the growth of an Al-rich oxide scale on top of the Cr–Al–O–N coating. However, this oxide scale containing substantial voids cannot prevent the underlying coating from oxidation. Oxidation kinetics study illustrates that the oxidation activation energies of (Cr x Al 1−x )–O–N coatings with x = 1.00, 0.76, 0.58, 0.33, and 0 are 252.3, 305.2, 370.7, 303.8, and 297.7 kJ/mol, respectively. The best oxidation resistance was obtained by the (Cr 0.58 Al 0.42 )–O–N coating, whereas the Al-containing (Cr 0.33 Al 0.67 )–O–N coating showed inferior oxidation resistance owing to its high intrinsic oxygen fraction.

Improving the oxidation behavior of low expansion Ni + CrAlYNO coating systems by regulating the oxygen content

Influences of MCrAlY Coatings and TBCs on Oxidation Behavior of a Ni-Based Single Crystal Superalloy

Investigation on the Oxidation Behavior of the NiCrAlY Bond-Coat with Low Al Content Sprayed by High Velocity Oxygen Fuel Method

Improved oxidation resistance of γ-TiAl intermetallics by sputtered Ni+CrAlYHfSiN composite coating

Microstructure and Oxidation Behavior of NiCoCrAlY Coating with Different Sm2O3 Concentration on TiAl Alloy

Study on Microstructure and Oxidation Resistance Mechanism of Y-modified NiCrAlY Coating Prepared by Pack Cementation

Oxidation behavior of laser remelted plasma sprayed NiCrAlY and NiCrAlY–Al2O3 coatings

Microstructure, mechanical properties, and oxidation behavior of arc-evaporated Cr–Al–O–N coatings with various Cr/Al ratios

Oxidation behavior of AlCoCrFeNiSi x high entropy alloy bond coatings prepared by atmospheric plasma spray

Oxidation behavior at 1100 °C of NiCrAlY coatings deposited by various PVD techniques

Oxidation Behavior of Cast Ni3Al Alloys and Microcrystalline Ni3Al+5% Cr Coatings with and without Y Doping

Improved Oxide Spallation Resistance of Microcrystalline Ni-Cr-Al Coatings

Isothermal oxidation behavior of NiCoCrAlY/ZrO2 composite coating on γ-TiAl alloy

High-temperature performance of Pt-modified Ni-20Co-28Cr-10Al-0.5Y coating: Formation mechanism of Pt-rich overlayer and its effect on thermally grown oxide failure

Oxidation Behaviors of the NiCrAlY Bond Coats in the Thermal Barrier Coatings under External Loads

Oxidation Behaviour of Sputter-Depositedni–cr–al Micro-Crystalline Coatings

A study on the thermal cyclic behavior of NiCrAlY coatings via femtosecond laser remelting with high repetition rate

Evolution of oxide layer during high-temperature oxidation of NiCoCrAlY coating via laser cladding on 304 stainless steel

Comprehensive study on the microstructure evolution and oxidation resistance performance of NiCoCrAlYTa coating during isothermal oxidation at High temperature

Significantly Improving the Oxidation and Spallation Resistance of a MCrAlY Alloy by Controlling the Distribution of Yttrium

Comparative Study on the Initial Oxidation Behavior of Conventional and Nanocrystalline MCrAlY Coatings - Effect of Microstructure Evolution and Dynamic Mechanisms