Calcia-magnesia-alumino-silicate-induced degradation of (Gd0.9Yb0.1)2Zr2O7 thermal barrier coatings prepared by plasma spray-physical vapor deposition (PS-PVD)

Shan Li,Wenbo Chen,Lidong Zhao,Hongbo Guo

DOI: https://doi.org/10.1016/j.surfcoat.2022.129179

IF: 4.865

2023-02-01

Surface and Coatings Technology

Abstract:(Gd0.9Yb0.1)2Zr2O7 (GYbZ) coatings with quasi-columnar structure prepared by PS-PVD were isothermally exposed to Calcia-magnesia-alumino-silicate (CMAS) at T = 1300 °C for t0 = 0.1 h, t1 = 1 h, t2 = 10 h, and t3 = 100 h. The resistance of GYbZ coatings against the CMAS melt penetration was investigated by wetting test and the reaction products were analyzed by energy-dispersive X-ray spectroscopy (EDS). The results show that a dense reaction layer was formed after isothermal exposure for t1 = 1 h, and the thickness of the reaction layers was almost the same from t1 = 1 h to t3 = 100 h, which indicated that the penetration of CMAS was basically suppressed. The particles between columns played a significant role in the rapid generation of a large amount of CMAS barrier apatite layer which prevented the penetration of the CMAS melt in the axial direction. The main reaction products were Gd-apatite, fluorite and spinel of which the Gd-apatite slowly grew from “free-island” to “net-frame”.

physics, applied,materials science, coatings & films