In Situ Preparation of Mg-Al-Co Layered Double Hydroxides on Microarc Oxidation Ceramic Coating of LA103Z Magnesium-Lithium Alloy for Enhanced Corrosion Resistance

Ju-Mei Zhang,Xin Duan,An-Rong Hou,Jia-Cheng Li,Kai Wang,Hui Cai

DOI: https://doi.org/10.1007/s11665-021-06058-8

IF: 2.3

2021-07-23

Journal of Materials Engineering and Performance

Abstract:First, microarc oxidation (MAO) was performed on the surface of the LA103Z magnesium (Mg) alloy. Then, Mg-Al-Co layered double hydroxide (LDH) coatings were grown in situ on the surface of the MAO ceramic coating via hydrothermal treatment at different temperatures. Scanning electron microscopy (SEM), energy-dispersive spectrometry, and x-ray diffraction were used to characterize the microstructure, chemical composition, and phase formation of the composite coatings. The corrosion resistance of the coatings was investigated by the polarization curve and electrochemical impedance spectroscopy. The results indicated that Mg-Al-Co LDH nanosheets covered the surface of the MAO ceramic coating and tended to grow in the recessed area. As the hydrothermal treatment temperature increased, the size of the LDH sheets increased, and the distribution became denser. The electrochemical tests showed that the self-corrosion current density (8.3260 × 10−7 A·cm−2) of the composite coatings prepared at 90 °C possessed optimal corrosion resistance, which was two orders of magnitude lower than that of the MAO ceramic coating (2.3874 × 10−5 A·cm−2). The corrosion resistance of the composite coatings decreased as the preparation temperature increased (100, 110 °C). The Mg-Al-Co LDH coating significantly enhanced the corrosion resistance of the MAO ceramic-coated alloy by sealing holes and microcracks, but high temperature destroyed the internal structure of the composite coatings and reduced their corrosion resistance.

materials science, multidisciplinary