Abstract:In this study, the mechanical, microstructural, and crystallographic effects of ball-burnishing applied to Al 7075-T6 alloy at 0.15–0.30 mm penetration depth, 0.15–0.30–0.60 mm/rev changing feed rates and 100–200 rpm range were investigated. After the ball-burnishing processes were carried out in different parameters, surface roughness measurements were applied to determine the surface qualities, and hardness and impact energy tests were applied to characterise the mechanical properties. Dislocation density and texture coefficient values were calculated by determining the crystallographic properties using X-ray diffraction. It has been determined that the ball-burnishing process directly affects the surface roughness, depending on the increasing rotational speed and feed rate. As a result of microstructural investigations, the average grain size decreased with increasing amount of deformation on the sample surface. At 200 rpm ball-burnishing parameter, the surface hardness of the sample increased by approximately 41% compared to the initial state and was measured as 265 HV2. It was determined that the ball-burnishing process did not positively affect the impact of the toughness of the alloy. The reason for this is that the roughness and scratches on the surface caused by the ball-burnishing process have a notch effect, increasing the crack formation and propagation speed. Dans cette étude, on a investigué les effets mécaniques, microstructuraux et cristallographiques du brunissage à bille appliqué à l'alliage Al 7075-T6 à une profondeur de pénétration de 0.15-0.30 mm, un changement de vitesses d'alimentation de 0.15-0.30-0.60 mm/tour et une plage de 100 à 200 tr/min. Après complétion des procédés de brunissage à bille selon les différents paramètres, on a effectué des mesures de rugosité de surface pour déterminer les qualités de surface, et l'on a effectué des essais de dureté et d'énergie de frappement pour caractériser les propriétés mécaniques. On a calculé les valeurs de densité des dislocations et de coefficient de texture en déterminant les propriétés cristallographiques à l'aide de la diffraction des rayons X. Il a été déterminé que le procédé de brunissage à bille affectait directement la rugosité de la surface, en fonction de l'augmentation de la vitesse rotationnelle et de la vitesse d'alimentation. À la suite des examens microstructuraux, la taille moyenne des grains diminuait avec l'augmentation de la quantité de déformation sur la surface de l'échantillon. Au paramètre de brunissage à bille de 200 tr/min, la dureté de surface de l'échantillon augmentait d'environ 41% par rapport à l'état initial et était mesuré à 265 HV2. Il a été déterminé que le procédé de brunissage à bille n'avait pas d'effet positif sur la ténacité de l'alliage. La raison en est que la rugosité et les égratignures sur la surface résultant du procédé de brunissage à bille ont un effet d'entaille, augmentant la formation de fissures et leur vitesse de propagation.

Fatigue strength improvement of aluminum alloy with surface defect by ball burnishing

Study on the Surface Defect of Aluminum Alloy Hole Burnishing

Multi-roller Taper Burnishing of Internal Chamfers and Its Enhancement Mechanism on 7050 Aluminum Alloy

Current research status of influence of ball burnishing process on fatigue behavior: a review

Evolution and anti-fatigue mechanism of surface characteristics of Ti60 alloy induced by ball burnishing and shot peening during tensile-compression fatigue

Surface integrity and fatigue behavior of AISI 4340 steel after hybrid laser-ultrasonic assisted ball burnishing process

Study on the Surface Enhancement of Thin-Walled Metallic Materials Using a Novel Double-Side Burnishing Tool

Running-in performance of 7075 aluminum alloy strengthened by burnishing technology

Investigation of the effect of ball-burnishing treatment applied to Al 7075-T6 alloy on mechanical and crystallographic properties

Improvement in Fatigue Performance of 2024-T3 Al Alloy Via Single Toroidal Roller Burnishing

Effect of Surface Modification on the High Temperature Low Cycle Fatigue Performance of LPBF 316L Austenitic Steel

Effect of surface integrity on fatigue life of 7075-T6 aluminum alloy by combination of fine turning with hydrostatic deep rolling

Evaluation of optimized surface characteristics in non-rotational sliding ball burnishing

Multi-objective optimization of slide diamond burnishing parameters for enhanced fatigue resistance of AISI 52100 steel

Surface integrity of ball burnished bioresorbable magnesium alloy

A study of shot peening and spinning rolling on fatigue of Al 7075 alloy samples

Enhanced fatigue performance of aluminum alloy through surface strengthening treatment

Effects of process combinations of milling, grinding, and polishing on the surface integrity and fatigue life of GH4169 components

Effect of machined surface integrity on fatigue resistance of aluminum-silicon alloy ZL109

Surface layer properties and fatigue behavior in Al 7075‐T73 and Ti‐6Al‐4V

Surface Condition Evolution and Fatigue Evaluation after Different Surface Processes for TiAl47Cr2Nb2 Alloy