Abstract:Abstract Shot peening processes are commonly used for improving the fatigue properties of steels. Shot peening introduces a compressive residual stress field in the near surface of steel, which can reduce or stop the growth of fatigue cracks and improve fatigue properties. This study experimentally investigated the effect of shot peening on the fatigue properties of 50CrV4 steel alloys with different artificial surface defects. Drilling tools were used to introduce different artificial defects with root radii of 0.585 mm and 0.895 mm on the surface of unpeened samples. The shot peening was applied to the drilled and undrilled samples. Scanning electron microscopy (SEM) observations, micro-hardness and X-ray diffraction residual stress measurements were conducted to analyse the characteristics of the shot-peened and unpeened samples. The results show that the shot peening leads to the transformation of the retained austenite to martensite in the near-surface microstructure. The hardness rates of the surface and near surface both increase by 8% after the shot peening. The peened samples exhibit compressive residual stresses with a high degree of isotropy in the near surface. The fatigue properties of samples were experimentally evaluated by conducting 3-point bending tests. The results indicate that the shot peening improves the fatigue life of drilled and undrilled samples. For the defects with the root radius of 0.895 mm, the shot peening leads to a 500% improvement in the fatigue life compared to unpeened samples regardless of defect depth. For the defects with the root radius of 0.585 mm, the improvement in fatigue life is 40% for the defect depth of 0.2 mm compared to unpeened samples. The improvement increases to 60% and 200% by increasing the defect depths to 0.4 mm and 0.6 mm. The fatigue properties are linked to the changes in the features of defects mainly caused by the deformation hardening and compressive residual stress after shot peening.

Evolution and anti-fatigue mechanism of surface characteristics of Ti60 alloy induced by ball burnishing and shot peening during tensile-compression fatigue

A Study of the Back Stress and the Friction Stress Behaviors of Ti-6Al-4V Alloy During Low Cycle Fatigue at Room Temperature

Effect of surface high density twin microstructure induced by shot peening on the fatigue behavior of Ti-6Al-4V

Effects of Ultrasonic Shot Peening on Fatigue Behavior of TA15 Titanium Alloy Fabricated by Laser Melting Deposition

Dwell and Normal Cyclic Fatigue Behaviours of Ti60 Alloy

Surface Condition Evolution and Fatigue Evaluation after Different Surface Processes for TiAl47Cr2Nb2 Alloy

Investigation of Wet Shot Peening on Microstructural Evolution and Tensile-Tensile Fatigue Properties of Ti-6Al-4V Alloy

Effect of surface high-density twinned structure on the fatigue crack initiation of Ti-6Al-4V

High fatigue performance and microscopic mechanisms of in-situ TiB 2 /7050Al composite at different temperatures

Understanding the Relations between Surface Stress State and Microstructure Feature for Enhancing the Fatigue Performance of TC6 Titanium Alloy

In-situ warm shot peening on Ti-6Al-4V alloy: Effects of temperature on fatigue life, residual stress, microstructure and mechanical properties

Fatigue Improvement of Additive Manufactured Ti–TiB Material through Shot Peening

Microstructural effects on the high-cycle fatigue and fracture behaviors of Ti-6Al-4V alloy

Gradient microstructure and foreign-object-damaged fatigue properties of Ti6Al4V titanium alloy processed by the laser shock peening and subsequent shot peening

Effect of thermal exposure on the microstructure and mechanical properties of Ti60 alloy

Investigation of residual stress, stress relaxation and work hardening effects induced by shot peening on the fatigue life of AA 6005-T6 aluminum alloy

Effects of shot peening and artificial surface defects on fatigue properties of 50CrV4 steel

Experimental Study on the Effect of Shot Peening and Re-Shot Peening on the Residual Stress Distribution and Fatigue Life of 20CrMnTi

Fatigue Limit of Custom 465 with Surface Strengthening Treatment

Fatigue performance of medical Ti6Al4V alloy after mechanical surface treatments

Microstructural evolution and oxidation in α/β titanium alloy under fretting fatigue loading