Abstract:Laser shock peening (LSP) as an emerging surface peening technology that is widely used in aerospace manufacturing. The effect of laser shock peening on surface integrity and high cycle fatigue (HCF) and very high cycle fatigue (VHCF) properties of 2024-T351 aluminum alloy was investigated in this study. Accordingly, the surface roughness, surface topography, microstructural, microhardness and residual stress of specimens treated with two different LSP pulse energy levels (10 J and 20 J) were analyzed. Additionally, the HCF and VHCF test was performed by ultrasonic fatigue test system. The results showed that surface roughness Ra value and microhardness of LSP treated specimens increased by a maximum of 89.37% and 16.3% comparing to the untreated specimen, respectively. X-ray diffraction analysis also showed that subgrain sizes were refined to the nanoscale. Furthermore, high-level compressive residual stresses (the maximum value about −210 MPa with 700 μm thickness) were introduced to the surface layer of the specimens. The S-N curve results showed that LSP treatment reduced the fatigue life of specimens, and the higher the laser pulse energy, the more obvious the effect of reduction. The fatigue fracture of specimens was analyzed via scanning electron microscope and residual stress distribution map. It is observed that fatigue cracks are predominantly initiated at fractured secondary phase particle locations in a VHCF range for untreated specimens. However, for LSP specimens, surface and internal crack initiation mechanisms were both observed. Under low and intermediate stress levels, the tensile residual stresses (which coexists with the compressive residual stresses) initiated fatigue cracks from the interior of the specimens; under high-stress levels, fatigue cracks were initiated at the material surface.

Surface layer properties and fatigue behavior in Al 7075‐T73 and Ti‐6Al‐4V

Fatigue performance of medical Ti6Al4V alloy after mechanical surface treatments

The Effect of Laser Shock Peening (LSP) on the Surface Roughness and Fatigue Behavior of Additively Manufactured Ti-6Al-4V Alloy

Effect of Surface Modification on the High Temperature Low Cycle Fatigue Performance of LPBF 316L Austenitic Steel

Microstructure and Fatigue Performance of Hard Al Alloy Repaired by Supersonic Laser Deposition with Laser Shock Peening Treatment

Experimental and Numerical Studies of Fatigue Behavior of Ti6Al4V Alloy Treated by Laser Shock Peening

Investigating post-processing impact on fatigue performance in LPBF Ti6Al4V with heat treatment, high pressure heat treatment, and dry electropolishing strategies

Investigation of surface finish and fatigue life of laser Powder Bed fused Ti-6Al-4V

The role of peening processes as a pre‐treatment to anodizing on fatigue behavior of aircraft aluminum alloy

CHARACTERIZATION OF SURFACE, SUBSURFACE DAMAGE AND THEIR EFFECT ON FATIGUE LIFE AFTER MACHINING OF AEROSPACE-GRADE ALUMINUM ALLOY (Al 6082-T6)

The effect of laser shock peening on surface integrity and high and very high cycle fatigue properties of 2024-T351 aluminum alloy

Surface Condition Evolution and Fatigue Evaluation after Different Surface Processes for TiAl47Cr2Nb2 Alloy

Fretting fatigue life investigation of AL7075-T6 alloy coated by multilayer thin solid films of TiCr/TiN/CrN and Ti/Cr/TiN/Cr/CrN/TiCrN

Cumulative Fatigue damage of AA7075-T6 under Shot Peening and Ultrasonic Surface Treatments

Effect of Post-Processing Treatment on Fatigue Performance of Ti6Al4V Alloy Manufactured by Laser Powder Bed Fusion

Effect of Ultrasonic Shot Peening on Surface Mechanical and Wear Behavior of Aluminum 7075-T651 Alloy

Relationship between Stress State and Microstructure of 7B04 Aluminum Alloy Surface Fatigue Properties by Laser Shock Peening Improvement

Surface Treatment of Powder-Bed Fusion Additive Manufactured Metals for Improved Fatigue Life

Surface condition driven fatigue performance of laser powder bed fusion H13 steel

Effect of surface integrity on fatigue life of 7075-T6 aluminum alloy by combination of fine turning with hydrostatic deep rolling

Research on surface integrity of Ti-6Al-4V alloy with compound treatment of laser shock peening and shot peening