Abstract:The surface mechanical attrition treatment was taken to fabricate the gradient structure in AZ31 magnesium alloy sheet. Microstructural investigations demonstrate the formation of dual gradients with respect to grain size and orientation, where the microstructural sizes decreased from several microns to about 200 nm from center area to treated surface, while the c-axis gradually inclined from being vertical to treated plane towards parallel with it. According to tensile results, the gradient structured sample has yield strength of 305 MPa in average, which is increased by about 4 times when compared with its coarse-grained counterpart. Meanwhile, contrary to quickly failure after necking in most traditional magnesium alloys, the failure process of gradient structure appears more gently, which makes it has 6.5% uniform elongation but 11.5% total elongation. The further comparative tensile tests for separated gradient layers and corresponding cores demonstrate that the gradient structured sample has higher elongation either in uniform or in post-uniform stages. In order to elucidate the relationship between mechanical properties and deformation mechanisms for this dual gradient structure, the repeated stress relaxation tests and pole figure examinations via X-ray diffraction were conducted in constituent gradient layer and corresponding core, as well as gradient structured sample. The results show that the pyramidal dislocations in dual gradient structure are activated through the whole thickness of sample. Together with the contribution of grain-size gradient, more dislocations are activated in dual gradient structure under tensile loading, which results in stronger strain hardening and hence higher tensile ductility.

Effect of gradient grain structures on corrosion resistance of extruded Al–Zn–Mg–Cu alloy

Effect of grain size and crystal orientation on the corrosion behavior of as-extruded Mg-6Gd-2Y-0.2Zr alloy

Effect of grain size uniformity and crystallographic orientation on the corrosion behavior of Mg-2Zn-1Al bar

Effect of Microstructure on the Corrosion Behavior of as-cast and Extruded Mg–Sn–Y Alloys

Formation of abnormal coarse grains and its effects on corrosion behaviors of solution treated ZK60 Mg alloy

Elucidating the dependence of corrosion behavior and mechanical property on the grain structure of low-temperature as-extruded Mg–Zn–Ca–Zr alloy

Investigation on corrosion behavior and mechanical properties of an extruded Mg-Zn-Al-Sn-Mn alloy

Effect of Extrusion Process on Microstructure, Corrosion Properties, and Mechanical Properties of Micro-Alloyed Mg–Zn–Ca–Zr Alloy

Effect of quenching rate on the corrosion mechanism of coarse grain and fine grain layer in 2195 aluminum-lithium alloy extruded plates

Effects of grain boundary chemistry and precipitate structure on intergranular corrosion in Al-Mg-Si alloys doped with Cu and Zn

Effects of extrusion parameters on the microstructure, corrosion resistance, and mechanical properties of biodegradable Mg–Zn–Gd–Y–Zr alloy

Mechanical Properties and Deformation Mechanism of Mg-Al-Zn Alloy with Gradient Microstructure in Grain Size and Orientation

Precipitation hardening and intergranular corrosion behavior of novel Al–Mg–Zn(-Cu) alloys

Corrosion behavior of Al-6.8Zn-2.2Mg-Sc-Zr alloy with high resistance to intergranular corrosion

Effect of Intermittent Variable Rate Non-isothermal Aging on the Corrosion Resistance of Al-Zn-Mg-Cu Alloy

Effect of extrusion on the microstructure and corrosion behavior of Mg-Zn-Mn-(0, 1.5)Sr alloys in Hank’s solution

Enhancing the intergranular corrosion resistance and mechanical properties of Al–Mg–xSi–Cu–Zn alloys by synergistic intergranular and intragranular precipitation behaviors

Corrosion behavior and mechanical properties of extruded low-alloyed Mg−0.5Bi−0.5Y−0.2Zn alloy

Effect of a bimodal grain structure on corrosion behavior and tensile properties of low-alloyed Mg-1Bi-1Zn-1Ag alloy

Role of bimodal-grained structure with random texture on mechanical and corrosion properties of a Mg-Zn-Nd alloy

Effect of the Zn/Mg Ratio on Microstructures, Mechanical Properties and Corrosion Performances of Al-Zn-Mg Alloys