Abstract:<p>To simulate laminate delamination using least input parameters and with no iteration is still a challenge. As the laminate is essentially bonded from individual laminae by the matrix, there exists a matrix-layer between two adjacent lamina ones, and a delamination of them must be resulted from a matrix-layer failure. However, a three-dimensional finite element analysis indicates that the stresses of the matrix layer are generally so small that it cannot fail before one of the adjacent laminae assumes a failure. This contradiction suggests that there must be something missing from the elemental stresses of the matrix-layer near the delamination front. We introduce a modifying coefficient (MC) to the matrix-layer stresses, and the modified stresses are checked with a strength-failure criterion. Once a tensile or shear failure is attained, delamination occurs to the adjacent laminae. At any load step, either the layers of an element are completely bonded together or completely separated from each other. No iteration is necessary to identify a delamination in the element. Only an additional critical energy release rate from a DCB test is required. Reasonable correlation between predicted delamination propagations and free-edge delamination initiations and measured counterparts of a number of laminates confirm the efficiency of this work.</p>

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to predict the occurrence of delamination in composite laminates without iterative calculations. Specifically, the paper proposes a non - iterative method to predict the delamination in composite laminates, which usually requires a large number of iterative steps in traditional finite element analysis (FEM). The main contributions of the paper are as follows: 1. **Iteration - free delamination prediction**: A method is proposed that can predict the delamination of laminates without any iteration. 2. **Stress correction of matrix - enriched layers**: A correction factor (MC) is introduced to correct the stress state of matrix - enriched layers, making it more in line with the actual stress distribution. 3. **Simplified input parameters**: Only the critical energy release rate (GIc) obtained from the double - cantilever beam (DCB) test needs to be additionally provided to complete the delamination prediction. ### Main problems - **Challenges in delamination prediction**: Traditional methods require a large number of input parameters when predicting delamination, and usually need multiple iterations to converge to a solution. - **Insufficient stress in matrix - enriched layers**: Traditional finite element analysis shows that the stress in matrix - enriched layers is usually very small, not sufficient to cause delamination, which is inconsistent with the actual situation. ### Solutions - **Introducing a correction factor**: By introducing a correction factor (MC), the stress of the matrix - enriched layer is corrected so that it can more accurately reflect the actual stress state. - **Strength failure criterion**: Using the corrected stress state, combined with the strength failure criterion (such as Tsai - Wu criterion), to determine whether delamination occurs. - **Iteration - free judgment**: In each load step, directly determine whether delamination occurs according to the corrected stress state without the need for iterative calculations. ### Experimental verification - **DCB test**: The effectiveness of the method was verified by the double - cantilever beam (DCB) test, and the results show that the prediction results are in good agreement with the experimental data. - **Free - edge delamination**: The prediction of free - edge delamination was also verified, and the results show that the method can reasonably predict the initiation and propagation of delamination. ### Formulas Some key formulas are used in the paper to describe the process of delamination prediction, for example: - **Tsai - Wu failure criterion**: \[ F=\left(\frac{\sigma_{11}}{F_{11}}+\frac{\sigma_{22}}{F_{22}}+\frac{\sigma_{33}}{F_{33}}+\frac{\sigma_{12}^{2}}{F_{12}^{2}}+\frac{\sigma_{13}^{2}}{F_{13}^{2}}+\frac{\sigma_{23}^{2}}{F_{23}^{2}}+\frac{\sigma_{11}\sigma_{22}}{F_{1122}}\right)\geq1 \] where \(\sigma_{ij}\) are stress components and \(F_{ij}\) are the corresponding failure strengths. - **Application of the correction factor**: \[ \sigma_{\text{mod}} = K_h\cdot\sigma \] where \(\sigma\) is the original stress, \(K_h\) is the correction factor, and \(\sigma_{\text{mod}}\) is the corrected stress. ### Conclusion The method proposed in the paper can effectively predict the delamination of composite laminates without iteration, simplifies the calculation process, and improves the efficiency and accuracy of prediction.

Prediction of laminate delamination with no iteration

Prediction of Laminate Delamination from Strength Failure of Interlaminar Matrix-Layer

Predicting delamination of hybrid laminate via stress modification on interlaminar matrix layer

A New Method to Predict Fatigue Life of Composite Laminate with Delaminating Effect Considered

Assessing delamination initiation from fiber and matrix properties

Failure Probability Prediction of Delamination under Cyclic Loading in Composite Laminates Using Cohesive Interface Elements

Modeling delamination growth in laminated composites

Application of a delamination model to laminated composite structures

A Semi-Analytical Method for Determining the Mode-I Delamination R-curve and Fiber Bridging Traction-Separation Law of Double-double Laminates

Assessing Delamination Initiation of Angle-Ply Laminates from Fiber and Matrix Properties

Analysis of Residual Compressive Strength of Composite Laminates with Delamination

Delamination Propagation Manipulation of Composite Laminates under Low-Velocity Impact and Residual Compressive Strength Evaluation

Physically based failure analysis method for laminated composites

Status of Numerical Simulation Methods for Delamination Damage of Composite Laminates

Failure prediction of an open-hole laminate under compression

Prediction of Delamination Buckling and Growth Behavior in Laminated Composites with Coexisting Delaminations

Assessing delamination initiation of laminates based on bridging model

An Extended Analytical Model for Predicting the Compressive Failure Behaviors of Composite Laminate with an Arbitrary Elliptical Delamination

Prediction of Delamination Growth in Laminated Structures Loaded by Quasi-static and Cyclic Loads

Failure Analysis of a Notched Laminate Through FE Approach

Dynamic Data Driven Load-Carrying Capacity Prediction Method for Composite Laminates with Delamination