Abstract:In order to meet the sealing demands of SiC heat exchanger, the Ni-Mo filler alloy was designed, prepared and employed to braze SiC ceramics. Wetting behavior of the Ni-Mo filler alloy on SiC ceramics and interfacial microstructure of the brazed joints were systematically characterized using optical observation furnace and XRD, SEM, EDS, TEM, respectively. Flexural strengths of the brazed joints at room temperature and high temperature were measured with four-point flexural strength method. HCl immersion test was performed to evaluate the corrosion resistance of the joints. The Ni-Mo filler alloy exhibited excellent wettability on SiC ceramics. During the process of brazing, SiC reacted with element Ni of the Ni-Mo filler alloy, resulting in the formation of Ni2Si + graphite reaction layer adjacent to the SiC substrate. Ni3Mo3C and Ni2Si compounds were precipitated at the center of brazing seam. When the brazing temperature increased from 1250 ℃ to 1400 ℃, the thickness of Ni2Si + graphite layer increased gradually. The maximum room-temperature flexural strength of 174 ± 33 MPa was obtained when brazed at 1300 ℃ for 40 min. The joints also exhibited stable high-temperature strength and acid corrosion resistance. When the test temperature was 700 ℃, 800 ℃, 900 ℃, the joints gave the strength retention rate of 92.5 %, 79.8 %, 67.2 %, respectively. It was believed that the formation of high melting point phases played an important role. Residual strength of the joints after HCl corrosion exceeded 130 MPa, revealing a good potential for applications in corrosion environment.

High‐strength SiC joints fabricated at a low‐temperature of 1400°C using a novel low activation filler of Praseodymium

Ultrafast low-temperature near-seamless joining of Cf/SiC using a sacrificial Pr3Si2C2 filler via electric current field-assisted sintering technique

Joining SiC ceramics with ZrSi2–SiC filler at low temperatures

Near-seamless joining of Cf/SiC composites using Y3Si2C2 via electric field-assisted sintering technique

Joining of SiC using CoFeCrNiCuTi high entropy alloy filler by electric current field assisted sintering

An ultra-strength SiC ceramic joint with an in-situ formed high-entropy carbide interlayer via diffusion bonding by spark plasma sintering

Microstructure and mechanical properties of SiC/SiC joints reinforced by in-situ growth SiC nanowires

Low temperature seamless joining of SiC using a Ytterbium film

Low temperature Pr 3 Si 2 C 2 ‐assisted liquid phase sintering of SiC with improved thermal conductivity

SiC fiber strengthened Si 14Ti high-temperature filler alloy for brazing SiC f /SiC and C/C composites

Reaction mechanism and mechanical properties of SiC joint brazed by in-situ formation of Ti3SiC2

Joining silicon nitride ceramics with ZrSi2-SiC composite filler by spark plasma sintering

Effects of the joining process on the microstructure and properties of liquid-phase-sintered SiC-SiC joints formed with Ti foil

Joining of SiC ceramics by combining NITE-SiC interlayer and its thickness control

Nano-infiltration and transient eutectic (NITE) joining of SiC ceramics applied for the harsh environments

A novel high entropy CoFeCrNiCu alloy filler to braze SiC ceramics

Joining of SiC ceramics using the Ni-Mo filler alloy for heat exchanger applications

Microstructure and Properties of Porous Si3N4/Dense Si3N4 Joints Bonded Using RE–Si–Al–O–N (RE = Y or Yb) Glasses

Joining of Ti-coated monolithic SiC using a SiCw/Ti3SiC2 filler by electric field-assisted sintering

Wetting and brazing of Cf/C composites with Si–Zr eutectic alloys: The formation of nano- and coarse-SiC reaction layers

Microstructure and properties of pressure-less joining of SiCf/SiC composites by Ti–Si alloys