Abstract:The ultrasonic-frequency pulse underwater wet welding (UFP-UWW) process was achieved through a constant-voltage-mode power source connecting an ultrasonic-frequency pulse power source in parallel. The arc voltage and welding current waveforms, sound signal variations, microstructural characteristics and mechanical properties at different parameters were investigated. The results showed that the ultrasonic-frequency pulse voltage and current of the UFP-UWW process displayed a periodic high-frequency oscillation on the based values of the conventional UWW process. The arc stability of the UFP-UWW process improved owing to the fact that the proportions of the unstable arc burning region could be reduced to 1.56% after the introduction of the ultrasonic-frequency pulse current. No significant changes in weld width and penetration were observed while the weld dilution rate increased to 54.2% for the combination of 40 V–30 kHz, compared with the results of the conventional UWW process. The flux-cored arc (FCA) welding arc in the air had the same frequency response to the ultrasonic excitation signal, which verified the existence of the ultrasonic-frequency vibration induced by the periodic high-frequency electromagnetic forces. The application of the ultrasonic-frequency pulse produced finer columnar grains in the welds with an average length of 315 μm, although the amount of pro-eutectoid ferrite and acicular ferrite varied little. The mechanical properties of the welded joints were also noticeably enhanced with the application of different ultrasonic excitation frequencies. The optimum tensile strength and impact toughness of the welded joint were improved by 6.7% and 21.7% when the applied ultrasonic excitation voltage was 40 V for a pulsed frequency of 30 kHz. These results facilitate the application of ultrasonic arc welding technology in the marine field.

Microstructure and corrosive-wear resistance of surfacing layers for underwater wet welding

Microstructure and Corrosion Behaviour of WC-Co Coating Fabricated by Plasma Arc Welding

The Corrosion Resistance of 0cr19ni9 Stainless Steel Arc Welding Joints with and Without Arc Surface Melting

Corrosion Resistance and High Temperature Wear Behavior of Carbide-Enhanced Austenite-Based Surfacing Layer Prepared by Twin-Wire Indirect Arc Welding

Corrosion resistance of stainless steel layer prepared by twin-wire indirect arc surfacing welding

Probing the Anti-Corrosion Behavior of X65 Steel Underwater FSW Joint in Simulated Seawater

Evaluation of Arc Signals, Microstructure and Mechanical Properties in Ultrasonic-Frequency Pulse Underwater Wet Welding Process with Q345 Steel

Microstructure and Mechanical Properties of Ultrasonic Assisted Underwater Wet Welding Joints

Effect of Water Flow on the Microstructure, Mechanical Performance, and Cracking Susceptibility of Underwater Wet Welded Q235 and E40 Steel

Microstructure and Mechanical Properties of an Underwater Wet Welded Dissimilar Ferritic/Austenitic Steel Joint

Microstructure Evolution Of E40 Steel Weldments In Ultrasonic-Wave-Assisted Underwater Fcaw

Microstructure and Mechanical Properties of Underwater Wet Welded High Carbon-Equivalent Steel Q460 Using Austenitic Consumables

Investigating the Advantages of Ultrasonic-assisted Welding Technique Applied in Underwater Wet Welding by In-Situ X-ray Imaging Method

Microstructure and Mechanical Properties of Underwater Laser Welding of Titanium Alloy.

The Abrasive Wear Resistance of Coatings Manufactured on High-Strength Low-Alloy (HSLA) Offshore Steel in Wet Welding Conditions

Microstructural Evolution and Its Effect on Mechanical Performance of Joint in Underwater Friction Stir Welded 2219-T6 Aluminium Alloy

Characterization of the underwater welding arc bubble through a visual sensing method

Effect of Parameters Change on the Weld Appearance in Stainless Steel Underwater Wet Welding with Flux-Cored Wire

Microstructure and mechanical properties of underwater friction stir welding of CNT/Al-Cu-Mg composites

Cucr1 Alloy Surface Hardening Via Ultrasonic Assisted Electro-Spark Deposition

Microstructure and properties of underwater laser welding of TC4 titanium alloy