Experimental Study on the Microstructure and Tribological Properties of Laser-Clad Ni60-WC Composite Coatings
Yupeng Cao,Kai Yan,Weidong Shi,Rui Zhou,Bin Li,Jiaxin Qin
DOI: https://doi.org/10.3390/ma17184638
IF: 3.4
2024-09-22
Materials
Abstract:To address the wear issues faced by the leg components of offshore platforms in harsh marine conditions, a Ni60-WC composite coating was fabricated on the surface of E690 high-strength steel using laser cladding. The microstructure, elemental distribution, microhardness, and tribological properties of the composite coating were characterized and tested using XRD (X-ray diffraction), SEM (scanning electron microscopy), EDS (energy-dispersive spectrometry), a microhardness tester, and a multifunctional tribometer. The study focused on the microstructure and tribological properties of the Ni60-WC composite coating. The results show that the composite coating primarily consists of γ-(Fe, Ni), WC, W2C, M23C6, and M6C phases, with cellular and dendritic structures at the top. WC and W2C, along with M23C6 and M6C, are precipitated from the W and C elements. The average hardness of the composite coating reached 569.5 HV, representing a 103% increase over the substrate hardness. The prepared composite coating exhibited a 32.6% increase in corrosion potential compared to the substrate. Additionally, the corrosion current density was reduced by 62.0%, indicating a significant enhancement in the corrosion resistance of the composite coating. The friction coefficient of the composite coating was reduced by 17.4% compared to the substrate, and wear volume was reduced by 79%, significantly enhancing the tribological performance of the coating due to reduced abrasive wear and fatigue wear.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering