Microstructure and Erosional Behavior of Erosion-Resistant Coatings of Super-Critical Boiler Pipes

LIU Shao-guang,WU Jin-ming,ZHANG Sheng-cai,HU Xiao-hai,RONG Shu-jie,LI Zhi-zhang

DOI: https://doi.org/10.3969/j.issn.1674-7607.2006.06.031

2006-01-01

Abstract:Two kinds of wire,core-charged with composite TiAl_3(AW1) and Cr_3C_2(AW2) powder,have been developed,to be used for building up corrosion-resistant coatings of super-critical boiler pipes,by means of supersonic arc-spraying technique.Coating's microstructure and its Erosional behavior under high temperature conditions have been studied and compared with those of steel 20 by using optical microscopy,Vicker-Hardness measurements,X-ray refraction observation,scanning electron microscopy and energy dispersion spectrum analysis.Results show that both AW1 and AW2 coating are structurally featured by consisting of successive layers,alternatively containing solid solution phases and oxide phases.Experimental results show that,after having been exposed to a 800℃ oxidation test,lasting 150 hrs,the oxidation resistance capability of AW1 and AW2 are respectively 10 and 15 times that of steel 20;the coating's erosion rates of steel 20,AW1 and AW2 all attained a maximum when the erosion attack angle is around 15° or 45°;the erosion resistances of AW1 and AW2 are found respectively to be 3.1 to 3.0 times that of steel 20.Figs 4,tables 2,and refs 6.