Abstract:The need for 2219 aluminum alloy and 2195 Al–Li alloy dissimilar friction stir welding (FSW) arises as the conventional 2219Al alloy was gradually replaced by the novel 2195Al alloy in fabrication of fuel tanks. However, the systematic investigation about the effect of welding parameters and material positioning on the microstructure evolution and mechanical properties of dissimilar FSW 2219Al/2195Al joints is lacking. In the present study, 2219Al-T8/2195Al-T8 plates were subjected to FSW under rotation rates of 800–1200 rpm and welding speeds of 200–800 mm min −1 with placing 2219Al-T8 alloys on the advancing side (AS) and retreating side (RS), respectively. The results showed that sound FSW joints were obtained under all the welding conditions. Welding parameters and material positioning affected the joint strength and fracture failure behavior. The FSW thermal cycle resulted in low hardness zones (LHZs) on both the 2219Al-T8 and 2195Al-T8 sides. The LHZ on the 2219Al-T8 side, characterized by partial coarsening of θ ′ (Al 2 Cu) precipitates and dissolution of the residual precipitates, showed the minimum hardness in the entire FSW joints. When 2219Al-T8 alloy was placed on the AS, the LHZ on the 2219Al-T8 side experienced higher peak temperature, and therefore more dissolution of θ ′ than that on the RS, thereby obtaining higher tensile strength. The tensile strength of the FSW joints at room temperature and − 196 °C largely increased as the welding speed increased from 200 to 400 mm min −1 . The FSW joints presented much higher tensile strength at − 196 °C than that at room temperature under the identical welding parameters and material position. The FSW joints fractured along the LHZ on the 2219Al-T8 side during tension. For the bending testing, the up and down bending failure angles were about 91–117° and 88–109°, respectively, with the weak zone appearing in "S" line or HAZ on the 2195Al-T8 side.

Microstructure, MAO Performance, Interfacial Characteristics and Corrosion Behavior of FSW Joint of Al-Mg-Sc Alloy

Microstructure evolution of thermo-mechanically affected zone in dissimilar AA2024/7075 joint produced by friction stir welding

Effect of Microstructure Evolution on Corrosion Behavior of 2195 Al-Li Alloy Friction Stir Welding Joint

Microstructure Evolution and Mechanical Properties of Friction Stir Welded Al–Cu–Li Alloy

Microstructure and Mechanical Behavior of Friction Stir-Welded Sc-Modified Al-Zn-Mg Alloys Made Using Different Base Metal Tempers

Microstructure, mechanical properties and corrosion of friction stir welded 6061 Aluminum Alloy

Microstructure and abnormal mechanical properties under the coupling effect of strain and temperature for friction-stir-welded joints of Al-Mg-Si alloy

Microstructure, microhardness and mechanical behavior of dissimilar AA7075/AA6061 alloys under friction stir welding

Friction stir welding of a rapidly solidified thin-strip continuous cast AA5182 Al–Mg alloy: analysis of microstructure evolution, mechanical properties, and corrosion resistance

Microstructure, mechanical and fracture properties of friction stir welded 2195 Al-Li alloy joints

Strengthening mechanism and corrosion behavior of friction stir welded LAZ933 magnesium-lithium alloy

Analysis of the Microstructure and Properties of Friction Stir Weld Zones in the Al 2139‐T8 Alloy

Effect of material flow behavior on the formation of interfacial reaction layers and fatigue performance of dissimilar friction stir welded S45C and AA6061-T6

Microstructural and mechanical properties of Al–Mg–Si–Cu joint fabricated by rotary friction welding

Dissimilar friction stir welding of 2219-T8 and 2195-T8 aluminum alloys: part I—microstructure evolution and mechanical properties

Microstructure and Mechanical Performance of FSWed Joint of T2 Copper and AA 1061

Effect of Microstructure Evolution on Corrosion Behavior of Friction Stir Welded Joint for 2195-T8 Alloy

Effects of Zr interlayer on microstructure, mechanical property and corrosion behavior of Al/Mg dissimilar friction stir welding lap joints

Study on corrosion resistance of HAZ and TMAZ in friction stir welding joint of 7075 aluminum alloy by thermal simulation

Material Flow Behavior and Thermal Cycle during Friction Stir Welding of AA5083/AZ91 Dissimilar Metals

Microstructure, properties and natural ageing behavior of friction stir welded dual-phase Mg-Li alloy