Friction stir welding of a rapidly solidified thin-strip continuous cast AA5182 Al–Mg alloy: analysis of microstructure evolution, mechanical properties, and corrosion resistance

Hesam Pouraliakbar,Hamed Jamshidi Aval,Ramezanali Farajollahi,Andrew Howells,Mark Gallerneault,Vahid Fallah

DOI: https://doi.org/10.1007/s00170-024-14020-w

IF: 3.563

2024-07-19

The International Journal of Advanced Manufacturing Technology

Abstract:This research explores the evolution of microstructure, mechanical properties, and resistance to corrosion in friction stir welds (FSW) of rapidly solidified continuously cast thin-strip (TS) AA5182 Al–Mg alloy. The same FSW procedures were applied to direct chill (DC) cast alloy samples of similar chemical composition with rolled and annealed microstructures to provide a basis for comparison. This study investigates the effect of the initial microstructure and manufacturing process on the weld characteristics. The findings indicate that performing FSW on annealed DC samples with a pin rotational speed of 400 rpm and a traverse speed of 160 mm/min results in the largest stir zone area (27.3 mm 2 ) and grain size (20.4 ± 3.1 μm). The results highlight the significant impact of temperature during FSW on the grain size within the stir zone. The combined influence of heat generation and severe plastic deformation during FSW leads to the development of a random crystallographic texture in the stir zone of AA5182 alloy specimens. In contrast to the as-cast TS and as-rolled DC samples, applying FSW to the annealed DC sample induces the formation of the β-Al 3 Mg 2 phase within the stir zone. Moreover, the formation of finer equiaxed grains in the stir zone of the TS sample contributes to an increased hardness compared to the base metal. The study concludes that conducting FSW on the as-cast TS AA5182 alloy sample yields the most favorable combination of hardness, strength, and corrosion resistance when compared to both as-rolled and annealed DC AA5182 alloy samples. Furthermore, it is emphasized that microstructural changes have a more pronounced impact on the corrosion behavior of Al–Mg alloys than the residual stress generated by FSW.

engineering, manufacturing,automation & control systems