Analysis of the Microstructure and Properties of Friction Stir Weld Zones in the Al 2139‐T8 Alloy

t sano,uchechi okeke,jian yu,c j boehlert,chianfong yen,tms

DOI: https://doi.org/10.1007/978-3-319-48237-8_66

2014-01-01

Abstract:The welding process introduces heat, plastic deformation, and chemical variation into the weld joints and modifies the microstructure, strength, and ductility of the welded region. Samples from two plates of Al 2139-T8 alloys welded together by friction stir welding (FSW) were examined. The microstructure of the stir zone (SZ), thermomechanical affected zone (TMAZ), and the unaffected base alloy were evaluated by scanning electron microscopy (SEM) and electron backscattered diffraction. The deformation and quasi-static tensile behavior of the samples from the SZ, TMAZ, and unaffected base alloy were examined by in-situ tensile experiments in the SEM, at room temperature and at 300 degrees C. The SZ samples showed higher elongation to failure and the unaffected base alloy exhibited the least amount of elongation. The ultimate tensile strength was determined to be lower in the TMAZ, and the yield strength increased away from the FSW region. The higher temperature tensile experiments showed a significant reduction in strength. The full results of the effect of the FSW on the Al2139-T8 microstructure and tensile behavior will be discussed in detail.