The Effect Of The Variation Of Microstructure In The Friction Stir Welded Zone On The Strain And Tensile Properties Of Al2139

t sano,jian yu,richard chen,chianfong yen

DOI: https://doi.org/10.1007/978-3-319-48761-8_95

2012-01-01

Abstract:The friction stir welding process creates three distinct zones; the weld nugget, themo-mechanically affected zone, and the heat affected zone. These zones have varying microstructure, texture, amounts of plastic deformation and dynamic recrystallization. The elevated local stresses and non-uniform strains under tension are attributed to the inhomogeneity in the weld. The ultimate tensile strength (UTS), yield stress, and elastic modulus were determined by tensile tests of samples in three orthogonal orientations from inside and outside the weld. The samples from inside the weld showed lower UTS and yield strength, but longer elongation than those from outside the weld. Digital image correlation was used to map the strain variations of the samples during the tensile tests. In addition, electron backscattered diffraction was used to determine the grain size and texture variation of the grains in the weld zones. The correlation of the microstructure variation on the tensile properties will be discussed.