Abstract:In this study, A356 matrix and 0.2 vol%∼0.8 vol% in-situ Al2O3p/A356 composite were hot rolled to 75% reduction ratio and 0.6 vol% composite was hot rolled to 75% and 83% reduction ratios. Scanning electron microscope (SEM), Electron back scattering diffraction (EBSD) and transmission electron microscopy (TEM) were used to characterize the microstructure and texture evolution so as to investigate the effect of the particle content and reduction ratios. In the 75% rolling reduction, the Si phase in the A356 matrix and Al2O3p/A356 composites was fragmented and distributed along the rolling direction (RD), obvious Al2O3 agglomeration diminished. On the state of 75% reduction, when the content of Al2O3 was 0.2 vol%, the composite had the finest grain size, however the 0.6 vol% composite had a better Si phase and Al2O3 distribution. The Al2O3 particle in 0.2 vol% sample can enhance the dislocation density and accelerate the sub-grain boundary formation. For the 75% reduction materials, the tensile properties increased with increase of particulate content to 0.6 vol% then decreased. The mechanical properties of 83% rolling reduction sample was better than the 75% reduction. Tensile tests showed that the ultimate tensile strength (UTS), yield strength (YS) and elongation (El) of 0.6 vol% Al2O3p/A356 composite increased to 282 MPa, 221 MPa and 17.5%, respectively, due to the uniform distribution of the particles and refined Si phase upon increasing the rolling reduction to 83%, in combination with T4 heat treatment. In addition, the mechanisms of particle dispersion, recrystallization grain refinement and strengthening are also discussed.

Effect of reduction rate on microstructure and properties of laminated steel/aluminium low density composites prepared by hot pressing

The Influence of Warm Rolling Reduction on Microstructure Evolution, Tensile Deformation Mechanism and Mechanical Properties of an Fe-30Mn-4Si-2Al TRIP/TWIP Steel

Microstructure and mechanical properties of Ti6Al4V based laminated composites at various rolling reductions

Interfacial microstructure and strengthening mechanism of stainless steel/carbon steel laminated composite fabricated by liquid-solid bonding and hot rolling

Effect of hot rolling on microstructures and mechanical properties of SiC p /A356 aluminum matrix composites

Effect of Cooling Rate on Microstructure and Mechanical Properties of a Microlaminated Low-Density Steel

Microstructure study of hot rolling nanosized in-situ Al2O3 particle reinforced A356 matrix composites

Study on the microstructure of AA6016/AA7050/AA6016 laminated composites based on Murty and Prasad instability criterion

Study on the Influence of Prefabricated Aluminum Layer Technology on the Properties of Corrugated Interface Steel/Aluminum/Aluminum Alloy Composite Panel

Characterization and Formability of Titanium/Aluminum Laminate Composites Fabricated by Hot Pressing

Enhanced Mechanical Properties of Ti/Mg Laminated Composites Using a Differential Temperature Rolling Process under a Protective Atmosphere

Effect of cumulative deformation and interlayer mechanical properties on bonding strength of corrugated interface steel/aluminum composite plate

Effect of warm-rolling on the strength and ductility of multilayered composite steel

Effect of annealing treatment on the microstructure and mechanical properties of bulk nanostructured Ti/AZ61 composites prepared by hot pressing

Annealing coordinates the deformation of shear band to improve the microstructure difference and simultaneously promote the strength-plasticity of composite plate

EFFECTS OF HOT-ROLLING PROCESSES ON THE FRACTURE BEHAVIORS AND MECHANICAL PROPERTIES OF 2009Al/SiCp METAL MATRIX COMPOSITES

Impact of various heat treatment processes and welding speeds on the mechanical properties and microstructures of soft/hard composite joints

Hot deformation behaviour and interfacial characteristics of bimetal composite at elevated temperatures

Effect of rolling reduction rate on the forming of microstructures on the surface of 2024 aluminum alloy

Study on Microstructure Evolution and Strengthening and Toughening of Friction Stir Processed AA6082-4%Al3Zr In-Situ Composites

Influence of Preheating Temperature on the Microstructure and Mechanical Properties of 6061/TA1 Composite Plates Fabricated by AFSD