Annealing coordinates the deformation of shear band to improve the microstructure difference and simultaneously promote the strength-plasticity of composite plate

Peng Da Huo,Feng Li,Ye Wang,Rui Zhi Wu,Rong He Gao,An Xin Zhang

DOI: https://doi.org/10.1016/j.matdes.2022.110696

2022-07-01

Abstract:When rolling aluminum (Al)/magnesium (Mg)/aluminum (Al) composite plates with large reduction, there are often differences in the matrix structure and hard brittle properties of interfacial intermetallic compounds, which have a negative impact on the mechanical properties. Therefore, it is necessary to adjust the evolution of the diffusion layer and homogenize the internal structure of the metal plate by annealing to achieve the best performance. In this study, Al/Mg/Al composite plates were formed by hard-plate rolling (HPR) with a single pass of 60% reduction and annealed. The results show that the tensile strength (UTS) of rolled plate is 235.4 MPa and the elongation to failure (A) is 6.2%. It is found that after annealing at 300 °C for 1 h, the interface bonding property is suitable, the microstructure is gradually uniformly refined by the joint action of shear band expansion and twin induced static recrystallization, the UTS reaches 265.1 MPa. The A is increased by 18.5%. In conclusion, annealing treatment can significantly improve the microstructure and connection strength of hard-plate rolling Al/Mg/Al composite plates and provide scientific guidance and technical support for the forming and manufacturing high-performance lightweight composite plates.

materials science, multidisciplinary