Abstract:Carbon-fiber reinforced composites are made up of three different phases. Tensile or compressive deformation in the longitudinal (fiber) orientation is controlled by the fibers, leading to a linear stress strain response which ends abruptly when the fibers fail by tensile fracture or kinking in compression. Conversely, major non-linear deformations can develop under transverse compression or in-plane shear because deformation is controlled by the polymeric matrix and the interphase.In this paper, first the V-notched rail shear test was used to research the mechanical properties of composite under in-plane shear loading, and the fracture surfaces of failed specimens were examined using scanning electron microscopy (SEM). The broken samples showed a large residual shear displacement. For [0/90](8s) cross-ply laminate V-notched beam test, the failure mode is the interactions of intralaminar and interlaminar failure. The intralaminar interfacial debonding, matrix cracking and interlaminar degradation occurs in succession. Then a representative volume element (RVE) of fiber random distribution was established, with two dominant damage mechanisms-matrix plastic deformation and interfacial debonding included in the simulation by the extended Drucker-Prager model and cohesive zone model respectively. The simulation results clearly reveal the damage process of the composites and the interactions of different damage mechanisms. It can be concluded that the in-plane shear fracture initiates as interfacial debonding and evolves as a result of interactions between interfacial debonding and matrix plastic deformation. The progressive damage process and final failure mode of in-plane shear model which are based on constitute are very consistent with the observed result under SEM of V-notched rail shear test. Also a transverse shear model was established as contrast in order to comprehensively understand the mechanical properties of composite materials under shear loading, and the progressive damage process and final failure mode of composite under transverse shear loading were researched.

The in situ matrix cracking behavior in cross-ply laminates under out-of-plane shear loading

Micro Failure Analysis of Fiber Metal Laminates

Progressive failure analysis of 2D woven composites at the meso-micro scale

Concurrent Multiscale Modeling of In-Plane Micro-Damage Evaluation in Z-pinned Composite Laminates

In-situ effect in cross-ply laminates under various loading conditions analyzed with hybrid macro/micro-scale computational models

Micro-damage Initiation Evaluation of Z-Pinned Laminates Based on a New Three-Dimension RVE Model

Transverse crack evolution modeling of cross-ply laminates with a single layer of phantom node intraply elements for identically-oriented ply groups

Deformation and Fracture Mechanisms of Automated Fiber Placement Pre-Preg Laminates under Out-of-plane Tensile Loading

Microscopic Progressive Damage Simulation and Scale-Span Analysis of Cross-Ply Laminate Based on the Elastic–Plastic Theory

Matrix cracking of fiber-reinforced ceramic composites in shear

Effects of matrix cracks on delamination of composite laminates subjected to low-velocity impact

In Situ Observation and Modeling of Damage Modes in Cross-Ply Ceramic Matrix Composites

Microscopic Progressive Damage And Failure Analysis Of Carbon-Fiber Reinforced Composite Under Shear Loading

Simulation Study of the Damage Mechanisms Appearing in a Cross Ply Composite Material Loaded in Uniaxial Tension

Analytical modeling of fiber–matrix interface failure in unidirectional laminae subjected to in-plane shear loads

Elastic and Fracture Behavior of Three-Dimensional Ply-to-Ply Angle Interlock Woven Composites: Through-Thickness, Size Effect, and Multiaxial Tests

In-Plane fracture of laminated fiber reinforced composites with varying fracture resistance: experimental observations and numerical crack propagation simulations

Study of the effect of strain rate on the in-plane shear and transverse compression response of a composite ply using computational micromechanics

Meso/macroscale study on the shear failure of CFRP laminates considering fibre rotation

Initial Damage Induced by Thermal Residual Stress and Microscopic Failure Analysis of Carbon-Fiber Reinforced Composite under Shear Loading

In-plane shear properties and damage process of composites based on unit cell analytic model