Abstract:LiO–AlO–SiO (LAS) glass–ceramics for low temperature co-fired ceramics (LTCC) application were prepared by melting method, and the effects of MgO on the sinterability, microstructure, dielectric property, thermal expansion coefficient (CTE) and mechanical character of this glass–ceramics have been studied. The X-ray diffraction images represent that the main phase is β-spodumene solid solutions. And some ZrO and CaMgSiO phases in LAS glass–ceramics are detected. The LAS glass–ceramics without additive (MgO) sintered at 800° had the dielectric properties: dielectric constant (ε) of 5.3, dielectric loss (tanδ) of 2.97 × 10 at 1 MHz, CTE value of 1.06 × 10 K, bulk density of 2.17 g/cm, and flexural strength of 73 MPa. 5.5 wt% MgO-added LAS glass–ceramic achieves densification at 800° exhibited excellent properties: low dielectric constant and loss (ε = 7.1, tanδ = 2.02 × 10 at 1 MHz), low CTE (2.89 × 10 K), bulk density = 2.65 g/cm as well as high flexural strength (145 MPa). The results indicate that the addition of MgO is helpful to improve the dielectric and mechanical properties. The formation of CaMgSiO crystal phase with higher CTE leads to the increase of CTE value of LAS glass–ceramics due to the increasing MgO content, and the increase of CTE is favourable for matching with silicon (3.1 × 10 K). The prepared LAS glass–ceramics have the potential for LTCC application.

Sintering Behaviors, Microstructure and Properties of Li2O-Al2O3-SiO2 Glass-ceramics for LTCC Applications

Phase Evolution and Properties of Li2O-Al2O3-SiO2-Based Glass-Ceramic for LTCC Applications

Effects of TiO2 on Microstructures and Properties of Li2O–Al2O3–SiO2 Glass–ceramics for LTCC Substrates

Influences of ZrO2 on Microstructures and Properties of Li2O–Al2O3–SiO2 Glass–ceramics for LTCC Applications

Effects of MgO on properties of Li2O–Al2O3–SiO2 glass–ceramics for LTCC applications

Low-dielectric-constant LiAlO2 Ceramics Combined with LBSCA Glass for LTCC Applications

Microstructure and Properties of ZnO Doped Li2O–Al2O3–SiO2 Glass–ceramic for LTCC Applications

Effect of CaO Content on Structure and Properties of Low Temperature Co-Fired Glass–ceramic in the Li2O–Al2O3–SiO2 System

Properties and Crystallization Kinetics of Low Temperature Co-Fired Li2O-Al2O3-SiO2 Electroceramics

Low Temperature Sintering and Dielectric Properties of Ca- Ba-Al-B-Si-O Glass/Al_2 O_3 Composites for LTCC Applications

Sintering Behaviors and Thermal Properties of Li2SiO3-based Ceramics for LTCC Applications

Densification, Flexural Strength and Dielectric Properties of CaO-MgO-ZnO-SiO2/Al2O3 Glass Ceramics for LTCC Applications

Tailoring sintering kinetics and dielectric properties of Li2SiO3 ceramics by CaO–B2O3–SiO2 glass dopant for LTCC substrate applications

Microwave dielectric characterization and densification mechanism analysis of CaO‐B2O3‐SiO2 glass‐ceramic/Al2O3 composites for LTCC applications

Densification and Characterization of Sio2-B2o3-Cao-Mgo Glass/Al2o3 Composites for Ltcc Application

Effect of silica addition on microstructure, sintering behavior, and dielectric properties of borosilicate glass/alumina composites for LTCC application

Low Temperature Sintering Densification and Properties of CaO-B2O3-SiO2-ZrO2 Glass/ca0.99cu0.01sio3 Composites for LTCC Application

Low Temperature Sintering and Characterization of La2O3-B2O3-CaO Glass-Ceramic/labo3 Composites for LTCC Application

Sintering, densification and crystallization of Ca–Al–B–Si–O glass/Al 2 O 3 composites for LTCC application

Synthesis and Characterization of Borosilicate Glass/β-Spodumene/al2o3 Composites with Low CTE Value for LTCC Applications

Influences of Al2O3 content on crystallization and physical properties of LAS glass-ceramics prepared from spodumene