Abstract:In this study a kind of patent binary Mg-6 wt.%Zn magnesium alloy was investigated as degradable biomedical material. The results of in vitro degradation including electrochemical measurements and immersion tests in simulated body fluid (SBF) revealed that zinc could elevate both the corrosion potential and Faraday charge transfer resistance of magnesium and thus improve the corrosion resistance. XRD and EDS analysis proved that the corrosion products on the surface of Mg-Zn contained hydroxyapatite (HA), Mg (OH)(2) and other Mg/Ca phosphates, which could reduce the degradation rate. The degradation process of magnesium alloy and the mechanism of corrosion layer formation were also discussed in this work, i.e. the byproducts of degradation of magnesium, Mg(2+) and OH(-), reacted with the phosphate and Ca(2+) in the SBF, thus the corrosion layer containing HA, Mg(OH)(2) and other magnesium-substituted apatite precipitated in corrosion pits and covered the surface of magnesium alloy.The hemolysis test found that the hemolysis rate of Mg-Zn was 3.4%, which is lower than the safe value of 5% according to ISO 10993-4. For the cell culture experiments, after 2 h incubation the pre-osteoblastic cell MC3T3-E1 was able to adhere and spread on the corrosion layer of Mg-Zn alloy, indicating that despite the fluctuation of pH value of DMEM culture solution, Mg-Zn alloy could still support the earlier adhesion of pre-osteoblastic cells on the surface. Hemolysis and adhesion of cells display good biocompatibility of Mg-Zn alloy in vitro. (C) 2009 Elsevier B.V. All rights reserved.

In Vitro Corrosion Mechanism of Biodegradable Mg-Zn-Gd Alloy

Corrosion Mechanism of the As-Cast and As-Extruded Biodegradable Mg-3.0Gd-2.7Zn-0.4Zr-0.1Mn Alloys.

Structural characteristics and corrosion behavior of biodegradable Mg-Zn, Mg-Zn-Gd alloys

Corrosion behavior and microstructure of biomedical Mg-Zn-Mn-Gd alloys

Corrosion barriers induced by nano-heterogeneous structure in a biodegradable Mg Zn-based metal

Influence of Specific Second Phases on Corrosion Behaviors of Mg-Zn-Gd-Zr Alloys

Microstructure design for biodegradable magnesium alloys based on biocorrosion behavior by macroscopic and quasi-in-situ EBSD observations

Microstructure, Mechanical Properties, and in Vitro Corrosion Behavior of Biodegradable Zn-1Fe-xMg Alloy

Microstructure, Mechanical Properties, and Corrosion Behavior of Degradable Mg-Al-Cu-Zn-Gd Alloys

Biocorrosion Behavior and Cytotoxicity of a Mg–Gd–Zn–Zr Alloy with Long Period Stacking Ordered Structure

Mechanical and Corrosion Properties of Mg-Gd-Zn-Zr-Mn Biodegradable Alloy by Hot Extrusion

A newly developed Mg-Zn-Gd-Mn-Sr alloy for degradable implant applications: Influence of extrusion temperature on microstructure, mechanical properties and in vitro corrosion behavior

Enhanced Antibacterial Properties, Biocompatibility, and Corrosion Resistance of Degradable Mg-Nd-Zn-Zr Alloy

In Vitro Corrosion of Mg-6zn-1mn-4sn-1.5nd/0.5y Alloys

Enhanced Mechanical Properties and Corrosion Resistance by Minor Gd Alloying with a Hot-Extruded Mg Alloy

Study on the Microstructure and Corrosion Behavior of Mg–(4 − X)gd–xy–2zn (x = 0, 2, 4 Wt%) Alloy

Corrosion resistance of ZrO 2 –Zr-coated biodegradable surgical magnesium alloy

Comparative Study on Corrosion Behavior and Mechanism of As-Cast Mg–Zn–Y and Mg–Zn–Gd Alloys

Influence of Ultra-Fine Grain Structure on Corrosion Behaviour of Biodegradable Mg-1Ca Alloy

Electrochemical Pourbaix Diagrams Of Mg-Zn Alloys From First-Principles Calculations And Experimental Thermodynamic Data

In Vitro Degradation, Hemolysis And Mc3t3-E1 Cell Adhesion Of Biodegradable Mg-Zn Alloy