High temperature oxidation behavior of porous MoAlB ceramic from 800 °C to 1100 °C in air
Junsheng Yang,Jie Li,Wenkang Liu,Siwei Tan,Gan Xiao,Baogang Wang,Yuzuo Liu,Shaoyun Song,Liu Yang,Xuejin Yang,Kui Yu
DOI: https://doi.org/10.1016/j.ceramint.2023.06.199
IF: 5.532
2023-07-01
Ceramics International
Abstract:MoAlB possesses the characteristics of both metals and ceramic materials, which has attracted extensive attention due to its excellent high-temperature oxidation resistance. For this reason, porous MoAlB is considered applicable to the practice of filtration under harsh environment. In this study, the high-temperature oxidation behavior of porous MoAlB ceramics is systematically studied at the temperatures ranging from 800 to 1100 °C. According to the results, the porous MoAlB exhibits good oxidation resistance at a maximum temperature of 1000 °C. The oxidation kinetics of porous MoAlB can be divided into three stages, and the estimated activation energies of the three stages are 253.83 kJ·mol−1, 367.48 kJ·mol−1 and 317.84 kJ·mol−1, respectively. In the stable stage at 1000 °C, the quadratic mass gain per unit area shows linearity over time, and the oxidation rate of porous MoAlB reaches 37.31 mg2·cm−4·h−1. As revealed by the analysis of the composition and microstructure of oxide layers, the main components of the oxide layer include MoO3, MoO2, Al2O3, B2O3. With the extension of oxidation time, the content of Al2O3 in the oxide films increases. The average pore size, permeability and open pore porosity of porous MoAlB show a trend of first decreasing and then tending to be stable. In addition, a discussion is conducted on the high-temperature oxidation mechanism of porous MoAlB.
materials science, ceramics