Abstract:Reducing the residual stresses and improving the mechanical strength of large-scale ceramic/metal brazing joints is an important problem that must be solved for its practical engineering application. Using composite filler with solid-state phase transformation ceramic particulates, it is theoretically feasible to relieve the residual stress and improve the mechanical properties of ceramic/metal brazed joints. In this study, Cu mesh, Ag-28Cu-2Ti (wt.%), and YSZ (0.6 mol.% Yttria-stabilized Zirconia solid-state phase transformation ceramic particulates) composite power fillers were used in the brazing of Ti3SiC2 ceramic and pure copper. The microstructure of joints and YSZ particulates in the interface was investigated and confirmed by SEM, EDS, STEM and TEM. In addition, the effect of YSZ particulates content on the mechanical properties of joints was investigated and evaluated by the shear strength. The results show that the interfacial phases were mainly Ti5Si3, TiC, TixCu, Ag (s, s), Cu (s, s) and YSZ particulates. Moreover, most of YSZ particulates undergo the solid-state phase transformation from t-ZrO2 to m-ZrO2 during the cooling process of brazing. The abnormal volume expansion of the solid-state phase transformation reduced the thermal mismatch between Ti3SiC2 ceramic and filler, thereby reducing the residual stress in the interface of joint. When using composite filler with 6wt.% YSZ particulates, the shear strength of Ti3SiC2/Cu joint reached the maximum. The maximum average shear strength of the joints was 80.2 MPa, which was about 103.6% more than the joint without YSZ particulates.This article is protected by copyright. All rights reserved

High Dislocation-Density Silver Particle Interlayer for High-Quality YSZ and Al2O3 Joints

Silver Particle Interlayer with High Dislocation Density for Improving the Joining of BaZr0.1Ce0.7Y0.1Yb0.1O3-δ Electrolyte and AISI 441 Interconnect

Micro-Ag Particle Interlayer with High Dislocation Density for Sintered-Joining of Al2O3 and AlN in Air

Joining 3YSZ Electrolyte to AISI 441 Interconnect Using the Ag Particle Interlayer: Enhanced Mechanical and Aging Properties

Reactive air brazing of YSZ ceramic with novel Al2O3 nanoparticles reinforced Ag-CuO-Al2O3 composite filler: Microstructure and joint properties

Joining YSZ Electrolyte to AISI 441 Interconnect for Solid Oxide Cells Using the Ag Interlayer: Enhanced Mechanical and Aging Properties

Reactive Air Brazing of Ysz-Electrolyte and Al2o3-Substrate for Gas Sensor Sealing: Interfacial Microstructure and Mechanical Properties

Brazing YSZ ceramics by a novel SiO2 nanoparticles modified Ag filler

Y2W3O12@SiO2 Composite Particles for Regulating Thermal Expansion and Interfacial Reactions in BaZr0.1Ce0.7Y0.1Yb0.1O3-δ/AISI 441 Joints

Joining of Yttria Stabilised Zirconia to Ti6Al4V Alloy Using Novel CuO Nanostructure Reinforced Cu Foam Interlayer

Exploring the role of Ag foam interlayer in alleviating the brittleness of G018 glass sealant for joining YSZ to Mn–Co spinel coated Crofer 22 H

Interfacial morphologies between alumina and silver-copper-titanium alloy

Wetting and Brazing of YIG Ceramics Using Ag–CuO–TiO2 Metal Filler

Evolution of microstructure and properties in reactive air brazing of 3YSZ ceramic and aluminized Crofer22h stainless steel using Pd-modified Ag–CuO filler

Improvement for Ti 3 SiC 2 /Cu joint brazed using composite fillers with abnormal expansion ceramic particulates

Interface Enhancing Strategy for Low-Temperature Bonding of Ag-based Nanoalloy

Interfacial microstructure and mechanical property of ZrC-SiC ceramic and TiAl joint brazed with AgZr active filler metal

Realizing the Air Joining of ZrO2 Ceramics Through Al Metal

Development of Ag@Si composite sinter joining with ultra-high resistance to thermal shock test for SiC power device: Experiment validation and numerical simulation

A Novel Ag–CuAlO2 Sealant for Reactive Air Brazing of 3YSZ and AISI 310S

The Effect of Interlayer Metals on the Strength of Alumina Ceramic and 1cr18ni9ti Stainless-Steel Bonding