Abstract:The oxide layer formed by ultra‐high melt point oxides (ZrO2, HfO2) and SiO2 glassy melt is the key to the application of traditional thermal structural materials in extremely high‐temperature environment. However, the negative effect of ZrO2 and HfO2 phase transitions on the stability of oxide layer and rapid volatilization of low viscosity SiO2 melt limit its application in aerospace. In this study, the ablation behavior of Cf/(CrZrHfNbTa)C‒SiC high‐entropy composite was explored systematically via an air plasma ablation test, under a heat flux of 5 MW/m2 at temperatures up to 2450°C. The composite presents an outstanding ablation resistance, with linear and mass ablation rates of 0.9 μm/s and 1.82 mg/s, respectively. This impressive ablation resistance is attributed to the highly stable oxide protective layer formed in situ on the ablation surface, which comprises a solid skeleton of (Zr, Hf)6(Nb, Ta)2O17 combined with spherical particles and SiO2 glassy melt. The irregular particles provide a solid skeleton in the oxides protective layer, which increased stability of the oxide layer. Moreover, the spherical particles have a crystal structure similar to that of Ta2O5 and are uniformly distributed in SiO2 glassy melt, which hinder the flow of SiO2 glassy melt and enhance its viscosity to a certain degree. And it reduces the volatilization of SiO2. In summary, the stable oxide layer was formed by irregular particles oxide and the SiO2 glassy melt with certain viscosity, thereby resulting in the impressive ablation resistance of the composite. This study fills a gap in ablation research on the (CrZrHfNbTa)C system.

Preparation and Ablation Behavior Analysis of Non-Equimolar C F /(hf 1/2 Zr 1/ 3 Ti 1/6 )C Composites under Oxyacetylene Flame with Different Heat Fluxes

Preparation and ablation behavior analysis of non-equimolar Cf/(Hf1/2Zr1/3Ti1/6)C composites under oxyacetylene flame with different heat fluxes

Ablation behavior and mechanisms of Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C–SiC high-entropy ceramic matrix composites

Ablation Behavior of Medium Entropy Carbide Ceramics with Different Molar Ratios of (hf, Zr, Ti)C in Oxyacetylene Flame

Microstructure and Ablation Behavior of C/C–HfC Composites Prepared by Precursor Infiltration and Pyrolysis

Ablative Property of C/C–SiC–HfC Composites Prepared Via Precursor Infiltration and Pyrolysis under 3,000 °C Oxyacetylene Torch

New Anti-Ablation Candidate for Carbon/carbon Composites: Preparation, Composition and Ablation Behavior of Y2Hf2O7 Coating under an Oxyacetylene Torch

Ablation Performances of Multi-Phased C/C-Zrc-Sic Ultra-High Temperature Composites

Ablation Resistant C/C-HfC-ZrC-TaC-SiC Composites Prepared by Reactive Melt Infiltration

Ablation resistance of C/C-HfC composites

Ablation behavior of a three-dimensional C/C-HfC composite prepared by a precursor infiltration and pyrolysis method

Ablation Mechanism of Carbon/Carbon Composites Modified by HfC–SiC in Two Conditions under Oxyacetylene Torch

Microstructure, Ablation Behavior and Thermal Retardant Ability of C/C-HfB2 Composites Prepared by Precursor Infiltration Pyrolysis Combined with Chemical Vapor Infiltration

Microstructure, thermophysical properties, and ablation resistance of C/HfC-ZrC-SiC composites

Ablation Behavior and Mechanism of C/C–ZrC–SiC Composites under an Oxyacetylene Torch at 3000°C

Mechanical and Ablation Properties of a C/C-HfB2-SiC Composite Prepared by High-Solid-loading Slurry Impregnation Combined with Precursor Infiltration and Pyrolysis

Preparation, Ablation Behavior and Thermal Retardant Ability of C/C-HfB 2 -Sic Composites

Microstructure Evolution and Phase Interface Characterization in Anti-Ablation (Hf1/4zr1/4ta1/4ti1/4)c-Coat Ed C/C Composites

Microstructure evolution and phase interface characterization in anti-ablation (Hf1/4Zr1/4Ta1/4Ti1/4)C-coated C/C composites

Ablation behavior and mechanisms of Cf/(CrZrHfNbTa)C‒SiC high‐entropy composite at temperatures up to 2450°C

Ablative and Mechanical Properties of C/C–ZrC Composites Prepared by Precursor Infiltration and Pyrolysis Process