Abstract:ZrC has high melting point and high hardness, and SiC-ZrC composite has excellent oxidation resistance properties. Using the toughening mechanisms of carbon fiber, C-f/ZrC-SiC ultra-high temperature Composite has become a researching focus in high-temperature materials. In this paper, the ratio of ZrC: SiC in the matrix was 2:1, 4:1, 8:1 and 16:1. The composite materials with SiC coating were tested with plasma wind tunnel ablation under the condition of 2700 K and 600 s, in order to assess the microstructures and ablation behaviors of different composite materials. The composition and microstructure of the ablated samples were characterized by XRD, SEM and EDS, respectively. The results show that at the central area at 2700 K, SiC on the surface is rapidly oxidized, while oxidation and ablation begin to occur in the matrix. The higher the Zr content in the matrix is, the better oxidation and ablation resistance are. The ablation layer is thick, even up to a millimeter level. As the Si content increases, it produces more SiO2 which is easy to volatilize under the surface. The porosity in the ablation layer increases due to evaporation of SiO2, and then oxygen will be easier to go to the interior, which result in more severe erosion. Meanwhile, oxidized ZrO2 from ZrC in the matrix is fewer. The protection of carbon fiber decreases, and it is the reason why the ablation of the carbon fiber is more serious.

Microstructure, thermophysical properties, and ablation resistance of C/HfC-ZrC-SiC composites

Microstructure and ablation behavior of C/C–HfC–SiC composites fabricated by reactive melt infiltration with Hf–Si alloy

Ablation Resistance and Thermal Conductivity of Carbon/Carbon Composites Containing Hafnium Carbide

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Ablation behavior of C/C–Zr1-xHfxC-SiC composites under an oxyacetylene flame at above 2500 °C

Ablation Resistant C/C-HfC-ZrC-TaC-SiC Composites Prepared by Reactive Melt Infiltration

Microstructure and Ablation Behavior of C/C–HfC Composites Prepared by Precursor Infiltration and Pyrolysis

Ablation Resistance of Hf/Zr-based Multiphase Coating/matrix-Modified C/C Composites at Ultrahigh Temperatures

Preparation, Ablation Behavior and Thermal Retardant Ability of C/C-HfB 2 -Sic Composites

Oxidation And Ablation Resistance Of C-F/Zrc-Sic Ultra-High Temperature Composites

Microstructure and Ablation Behavior of Carbon/carbon Composites Infiltrated with Zr–Ti

Microstructure Evolution and Properties of Hf/Zr-based UHTCs Modified C/C Composites Prepared by Reactive Melt Infiltration Method

Microstructure and ablation resistance of C/C-HfC-SiC composites prepared by RMI with different powder particle sizes

Effect of SiC on the anti-ablation resistance and flexural strength of (Hf-Ta-Zr)C-C/C composites

Influences of deposition temperature, gas flow rate and ZrC content on the microstructure and anti-ablation performance of CVD-HfC-ZrC coating

Ablation resistance of C/C-HfC composites

Ablation Resistance of SiC–HfC–ZrC Multiphase Modified Carbon/carbon Composites

Ablation behavior and mechanism of C/C-HfC-SiC composites

The Microstructure, Ablative Resistance and Mechanical Properties of C/C-(Zr, V, Si)C Composites after Ablation

Microstructure, Ablation Behavior and Thermal Retardant Ability of C/C-HfB2 Composites Prepared by Precursor Infiltration Pyrolysis Combined with Chemical Vapor Infiltration

Microstructure and ablation behavior of C/C composites doped with ZrB2